Tunable photonic crystal device

ABSTRACT

This application describes a tunable photonic crystal device based on the electrical actuation of photonic crystal films. This device displays non-bleachable structural color, reflecting narrow bands of wavelengths tuned throughout the entire visible spectrum by expansion and contraction of the photonic crystal lattice

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a continuation-in-part of U.S. patent application Ser. No. 10/681,374 filed Oct. 9, 2003, entitled WIDELY WAVELENGTH TUNEABLE POLYCHROME COLLOIDAL PHOTONIC CRYSTAL DEVICE the entirety of which is hereby incorporated by reference.

Application Ser. No. 10/681,374 relates to, and claims the benefit of, U.S. provisional patent application Ser. No. 60/416,910 filed on Oct. 9, 2002, entitled WIDELY WAVELENGTH TUNEABLE POLYCHROME COLLOIDAL PHOTONIC CRYSTAL DEVICE, which is incorporated herein in its entirety.

FIELD OF THE INVENTION

The present invention relates to a tunable photonic crystal device. In particular, the tunable photonic crystal device can be controlled by applying an electrical potential between working and counter electrodes. The tunable photonic crystal device may incorporate the photonic crystal composite material disclosed in U.S. application Ser. No. 10/681,374.

U.S. application Ser. No. 10/681,374 discloses a composite photonic crystal material produced made of a cross-linked metallopolymer network composite film including microparticles which has an adjustable lattice dimension so that the wavelength of optically Bragg diffracted light originating from stop bands or higher energy bands of the composite film can be tuned. More particularly the Ser. No. 10/681,374 application provides a method of making widely wavelength tunable polychrome colloidal photonic crystal devices, referred to here also as a photonic crystal-gel material or a photonic crystal composite material, specifically a new type of 3-D Bragg diffractive optical element in the form of a film or patterned film or shape of any dimension or array of shapes of any dimension that has a continuously and finely, rapidly and reversibly, reproducibly and predictably, adjustable photonic crystal lattice dimension and concomitantly the predetermined ability to cause light of widely different wavelengths to be continuously and finely, rapidly and reversibly, reproducibly and predictably, and efficiently reflected or transmitted across the ultraviolet, visible and near infrared regions of the electromagnetic spectrum.

BACKGROUND OF THE INVENTION

Photonic crystals are an emerging class of materials, which interact with electromagnetic radiation through a periodic modulation in their refractive indices when the periodicity coincides with the scale of the radiation wavelength (see E. Yablonovitch, Phys. Rev. Lett. 58, 2059 (1987), and. S. John, Phys. Rev. Lett. 58, 2486 (1987)). Though for the moment they are objects of mostly fundamental scientific interest, photonic crystals will likely become increasingly prevalent in both basic and applied circles, furthering their potential for a myriad of proposed and unforeseen applications, (see: J. D. Joannopoulos, P. R. Villeneuve, Nature 386, 143 (1997)).

A particularly elegant method for fabricating these intricately structured materials involves the self-assembly of a collection of size-monodisperse spherical colloids into a long-range ordered lattice of well-defined geometry. Spherical colloids of both inorganic and polymeric composition have been studied exhaustively (see P. C. Hiemenz, R. Rajagopalan “Principles of Colloid and Surface Chemistry”, Marcel Dekker Inc., New York (1997)), can be routinely obtained as monodisperse suspensions, and are quite inexpensive to produce. Given these considerations, and recent success in assembling these colloids into face-centered cubic (fcc) crystals with very low defect concentration, it is not surprising that they have been thrust to the forefront of photonic crystal research (For recent reviews see (a) Y. Xia, B. Gates, Z-Y. Li, Adv. Mater. 13, 409 (2001); (b) V. L. Colvin, MRS Bull. 26, 637 (2001)).

The concept of a self-assembled colloidal photonic crystal, though a new one, has been successfully demonstrated many times, and a great variety of materials have been incorporated into these systems by templating against colloidal crystals or their replicas (arrays of air holes in dielectric media), see B. T. Holland, C. Blanford, A. Stein, Science 1998, 281, 538. Consequently, research in the area has begun to focus on designing systems not only composed of materials unexplored in this regard, but capable of being tuned in a variety of ways by external stimuli, K. Busch, S. John, NATO Sci. Ser., Ser. C: Math. Phys. Sci. 563, 41 (2001). The promise of this approach lies not only in being able to vary optical properties in a very controlled manner, but also in using the intricate light-microstructure interplay that creates structural color (that is, to be contrasted with color from pigments or chromophores) in these colloidal photonic crystal materials to effect accurate sensing with an easily measurable optical response.

One of the ways in which a colloidal photonic crystal can be tuned is via a mechanical response, that is, changing external conditions such that the crystal changes in shape or dimensions. Seminal studies in the experimental demonstration of this concept, using the volume changes of a swollen hydrogel have been made by Asher and coworkers, see J. M. Weissman, H. B. Sunkara, A. S. Tse, S. A. Asher, Science 274, 959 (1996). Their approach was to fix in a hydrogel matrix an array of highly charged latex microspheres self-assembled in a non-close packed array through mutually repulsive electrostatic interactions in a rigorously de-ionized medium.

These so-called polymerized crystalline colloidal arrays (PCCA's) could take advantage of the well-known properties of organic polymer acrylamide-based gels, (T. Tanaka, Phys. Rev. Lett. 40, 820 (1978)) as well as perform sensing functions by incorporating into these organic polymers receptors for specific analytes (J. H. Holtz, S. A. Asher, Nature 389, 829 (1997)). These systems are quite elegant, but suffer from a number of drawbacks such as poor mechanical stability due to high solvent content, slow response to stimuli, and the polycrystalline nature of the samples, which prevents them from being able to accurately control features of the Bragg optical diffraction peak, such as its wavelength, width and intensity.

Some researchers have taken the lead of Asher and co-workers and utilized the PCCA system and post-modified it to achieve a higher mechanical stability, (S. H. Foulger, J. Ping, A. C. Lattam, Y. Ying, D. W. Smith Jr., Adv. Mater. 13, 1898 (2001)) but this system still suffers from the same fundamental drawbacks as the original materials developed by Asher et al. Still others have used the same organic polymer hydrogels employed by these prior researchers and have incorporated them into close-packed colloidal crystals, resulting in a similar type of material simply made by a slightly modified route (Y. Takeoka, M. Watanabe, Langmuir 18, 5977 (2002)). The important point to note about this prior PCCA work is that the matrix that encapsulates the colloidal crystal is an organic polymer gel, which as amplified upon below is quite distinct in its composition and properties to the metallopolymer gels that may be used in the invention described herein.

Because photonic crystals reflect bright colors with potential tunability, they are useable as the active materials in refreshable full-color digital displays. To achieve this applicable, a difficult set of requirements must be met: electrical tunability, thin and homogenous oriented films, large tuning range, relatively rapid response time, mechanical and cycling stability, low voltage/current requirements, and the ability to implement the material into a feasible, practical, scalable and manufacturable device.

The photonic crystal materials useable in the present invention include planarized composite colloidal photonic crystals consisting of an ordered face centered cubic (fcc) arrangement of sub-micrometer size microspheres in a matrix of weakly cross-linked polyferrocenylsilane (PFS), whose cross-link density can be continuously and finely adjusted, a novel metallopolymer (also referred to in this application as an metallopolymer), which has the unique ability to function as a reversibly redox tunable, swellable-shrinkable metallopolymer gel, (K. Kulbaba, M. J. MacLachlan, C. E. B. Evans, I. Manners, Macromol. Chem. Phys. 202, 1768 (2001)). This class of reversibly redox tunable, swellable-shrinkable colloidal photonic crystal metallopolymer gel composite materials are entirely new—composites of this genre have never been made before nor reported before in the patent or open literature. They display unique chemical and physical properties because the metallopolymer gel matrix unlike all known organic polymer gels has metal atoms that are directly integrated into the backbone of the polymer. As a result of a polymer backbone comprised of metal atoms these metallopolymer gels overcome many deficiencies inherent in organic polymer analogues and also introduce additional and valuable functionality by virtue of the properties of the metal-backbone containing polymer used (I. Manners, Science 294, 1664 (2001)). Because this class of redox-active metallopolymers have well-defined, stable redox couples, the state of charge of the metallopolymer can be continuously, finely and reversibly changed in a straightforward manner, chemically or electrochemically, to effect a change in its interactions with a fluid medium. This can result in either a chemo-mechanically or electro-mechanically induced expansion or contraction of the colloidal photonic crystal lattice upon switching the metallopolymer gel to the oxidized or reduced state due to the variety of fluid media available.

Although there has been one previous report dealing with the electrochemical tunability of the optical properties of an inverse colloidal crystal made of tungsten trioxide, (Sumida, T.; Wada, Y.; Kitamura, T.; Yanagida, S. Chemistry Letters 2, 180 (2002)) it is important to note that this system is completely different to the one described in the present application in that tungsten trioxide is a solid state material and not a polymer and further the tunability of the optical colloidal photonic crystal properties arises from a classical metal-nonmetal induced refractive index change in the tungsten trioxide inverted colloidal photonic crystal matrix that occurs on electrochemically injecting lithium ions and electrons into the void spaces within the structure and conduction band respectively and not a change in colloidal photonic crystal lattice dimensions, which is the basis of the mode of operation of the metallopolymer gel colloidal photonic crystal composite materials in the embodiment described herein.

It would also be advantageous to provide an economical method of producing colloidal photonic crystal materials which are rapidly and reproducibly wavelength tunable.

SUMMARY OF THE INVENTION

This application describes a tunable photonic crystal device based on the electrical actuation of photonic crystal films. This device displays non-bleachable structural color, reflecting narrow bands of wavelengths tuned throughout the entire visible spectrum by expansion and contraction of the photonic crystal lattice.

In one aspect of the present invention, there is provided a tunable photonic crystal device comprising: a working electrode and a counter electrode forming a cell space therebetween; a conductive solution filling the cell space, the conductive solution comprising charged particles and a solvent; and a wavelength tunable photonic crystal film in the cell space, the material comprising: an ordered array of first constituents having a first refractive index embedded within a polymer network having a second refractive index different than the first refractive index, the ordered array of first constituents having a lattice spacing giving rise to a reflected wavelength, the polymer network being expandable and contractible in response to controlled uptake and expulsion, respectively, of at least one of the charged particles and the solvent by the polymer network, the reflected wavelength being dependent on the lattice spacing and the lattice spacing being tunable by expansion and contraction of the polymer network, the amount of uptake and expulsion of at least one of the charged particles and the solvent being tunable by controlling an electronic configuration of the polymer network; the device being adapted to be connected to an electrical source for applying an electrical potential between the working and the counter electrodes to control the electronic configuration of the polymer network.

In another aspect, there is provided a method of tuning the device described above, comprising: applying the electrical potential between the working electrode and the counter electrode to change the electronic configuration of the polymer network; and maintaining the electrical potential to tune the reflected wavelength from a first wavelength to a second wavelength.

In another aspect, there is provided discloses a display device comprising the tunable photonic crystal device described above.

The present application also describes a straightforward synthetic strategy for making a photonic crystal-gel material that is comprised of a composite material wherein the microstructure of the composite material is based upon an organized array of diffracting units, such as microspheres or voids, encapsulated within a redox active cross-linked metallopolymer network, where the term “cross-linked network” is used interchangeably with the word “gel” in this application.

In another aspect of the invention there is provided a wavelength tunable composite material, comprising: an ordered array of first constituents having a first refractive index embedded within a cross-linked metallopolymer network having a second refractive index different than the first refractive index, the ordered array of first constituents having a lattice spacing giving rise to Bragg diffraction when the composite material is illuminated, the cross-linked metallopolymer network being comprised of a polymer backbone including metal atoms chemically integrated therein, the cross-linked metallopolymer network having an electronic configuration dependant on the metal atoms, the metal atoms being switchable between more than one electronic configuration, the cross-linked metallopolymer network being expandable and contractible in response to controlled uptake and expulsion, respectively, of a selected fluid by the cross-linked metallopolymer network so that when the cross-linked metallopolymer network takes up the selected fluid it expands which shifts a Bragg diffraction wavelength to longer wavelengths and when the cross-linked metallopolymer network expels the selected fluid it contracts which shifts the Bragg diffraction wavelength to shorter wavelengths, the amount of fluid uptake and expulsion being controlled by controlling the electronic configuration of the cross-linked metallopolymer network.

In another aspect of the invention there is provided a method of wavelength tuning a composite material, comprising: a) producing an ordered array of first constituents having a first refractive index embedded within a cross-linked metallopolymer network having a second refractive index different than the first refractive index, the ordered array of first constituents having a lattice spacing giving rise to Bragg diffraction when the composite material is illuminated, the cross-linked metallopolymer network being comprised of a polymer backbone including metal atoms chemically integrated into the polymer backbone and connected together directly or through linking units, the cross-linked polymer network having an electronic configuration dependant on the metal atoms, the metal atoms being switchable between more than one electronic configuration, the cross-linked metallopolymer network being expandable and contractible in response to controlled uptake and expulsion, respectively, of a selected fluid by the cross-linked metallopolymer network so that when the cross-linked polymer network takes up the selected fluid it expands which shifts a Bragg diffraction wavelength to longer wavelengths and when the cross-linked polymer network expels the selected fluid it contracts which shifts the Bragg diffraction wavelength to shorter wavelengths, the amount of fluid uptake and expulsion being controlled by controlling the electronic configuration of the cross-linked polymer network; and b) switching the electronic configuration of the cross-linked metallopolymer network so that the cross-linked polymer network changes dimensions and modulates the lattice spacing of the ordered array of first constituents, which shifts the Bragg diffraction wavelength to a pre-selected wavelength.

The microspheres may be self-assembled into a colloidal photonic crystal and in such a way that the microspheres are not rigidly connected and the interstitial spaces of the colloidal photonic crystal lattice are filled to a certain extent with the cross-linked metallopolymer network. The polymer gel is selected so that it can be reversibly swollen or shrunken by a redox change or fluid (liquid or vapor) change applied to the metallopolymer-gel. The colloidal photonic crystal-metallopolymer gel composite material is in the form of a film or patterned film or shape of any dimension or an array of shapes of any dimension and the film or patterned film or shape of any dimension or array of shapes of any dimension has a controlled area and thickness with the film or patterned film or shape of any dimension or array of shapes of any dimension being grown upon the substrate and made adherent to thereto.

The substrate may be chosen to be electrically conducting or insulating and optically transparent or reflective or absorptive and the lattice dimensions of the colloidal photonic crystal-metallopolymer gel composite material may be redox adjustable or fluid adjustable in a continuous and fine, rapid and reversible, reproducible and predictable manner thereby providing a means for concomitantly tuning the wavelength of optically Bragg diffracted light originating from stop bands or higher energy bands through the adjustable lattice dimension colloidal photonic crystal metallopolymer gel composite film or patterned film or shape of any dimension or array of shapes of any dimension in a continuous and fine, rapid and reversible, reproducible and predictable fashion across the ultraviolet, visible and near infrared wavelength regions of the optical electromagnetic spectrum thereby providing a novel kind of chemo-mechanical and electro-mechanical broadly color tunable Bragg optical diffractive material whose polychrome optical functionality could find utility in wavelength tunable filter, mirror, multiplexor, compensator, limitor and switching optical telecommunication applications as well as optical sensing and optical imaging, display, fingerprinting and printing applications.

Another object of this invention is to describe a straightforward synthetic strategy that can effect the removal of the constituent microspheres from the aforementioned colloidal photonic crystal metallopolymer gel composite film to create a macroporous metallopolymer-gel photonic crystal film whose lattice dimensions may be redox adjustable or fluid adjustable in a continuous and fine, rapid and reversible, reproducible and predictable manner thereby providing a means for concomitantly tuning the wavelength of optically Bragg diffracted light originating from stop bands or higher energy bands from said macroporous metallopolymer-gel photonic crystal film in a continuous and fine, rapid and reversible, reproducible and predictable fashion across the ultraviolet, visible and near infrared wavelength regions of the optical electromagnetic spectrum thereby providing a novel and distinct type of chemo-mechanical and electro-mechanical broadly color tunable Bragg optical diffractive material whose polychrome optical functionality could find utility in wavelength tunable filter, mirror, multiplexor, compensator, limitor and switching optical telecommunication applications as well as sensing, imaging, display, printing and fingerprinting applications.

When microspheres are used they may have diameters in the range of 0.1 to 5 microns. The cross-linked polymer may be a lightly cross-linked polyferrocenylsilane (PFS).

The present invention incorporates the photonic crystal material disclosed in U.S. application Ser. No. 10/681,374, which provides a widely wavelength tuneable polychrome colloidal photonic crystal device, also referred to here as a photonic crystal-gel material or photonic crystal composite material or colloidal photonic crystal material, specifically a new type of 3-D Bragg diffractive optical element in the form of a film or patterned film or shape of any dimension or array of shapes of any dimension that has a continuously and finely, rapidly and reversibly, reproducibly and predictably, adjustable photonic lattice dimension and concomitantly the predetermined ability to cause light of widely 15′ different wavelengths to be continuously and finely, rapidly and reversibly, reproducibly and predictably, and efficiently reflected or transmitted across the ultraviolet, visible and near infrared regions of the electromagnetic spectrum. The tunable polychromicity of this colloidal photonic crystal material has utility in a myriad of applications requiring wavelength tunability of light, exemplified but not limited to optical components like filters, mirrors, multiplexors, compensators, limitors and switches of use in optical telecommunication systems as well as color tunable materials of use in imaging, display, printing, fingerprinting and sensing systems.

BRIEF DESCRIPTION OF THE DRAWINGS

The present invention will now be described in detail, by way of example only, reference being made to the accompanying drawings in which:

FIG. 1A a) shows the synthesis of a next generation cross-linker for the composite silica cross-linked metallopolymer (PFS) gel colloidal photonic crystal film. The cross-linker in the new PFS comprises two polymerizable silaferrocenyl rings appended to the two ends of an electrically conductive, pi-conjugated diethynylbenzene group. b) Single crystal x-ray structure determination of the product shown in the synthetic scheme. Note that the conductive cross-links in this next generation composite silica cross-linked metallopolymer (PFS) gel colloidal photonic crystal are designed to improve the swelling and shrinking time response to an electrochemical stimulus by increasing the rate of charge-transport within the film.

FIG. 1B shows a schematic of the process for material fabrication; (i) Evaporative deposition of silica colloids; (ii) 200° C., 12 hours, vacuum; (iii) Treatment with capping agent 1; (iv) Infiltration of monomers 2 and 3, removal of solvent at 300 mm Hg; (v) Sample covered with PTFE sheet, glass slide and bound with binder clips; (vi) 190° C., 13 hours, N₂; (vii) Careful removal of clips, PTFE and glass cover.

FIG. 2 shows a Scanning Electron Micrograph (SEM) image of a cross-section of the composite silica crosslinked metallopolymer (PFS) gel colloidal photonic crystal film showing the glass substrate, the infiltrated colloidal crystal, and the bulk metallopolymer (PFS) overlayer. The inset shows a magnified view of (111) crystal planes exposed during sample cleavage, confirming the face-centered cubic (fcc) arrangement of microspheres in these colloidal crystals.

FIG. 3( a) shows experimental transmission spectra of the same silica-cross linked gel colloidal photonic crystal soaked with solvents of different solubility parameter and refractive index. Circles: sample prior to solvent infiltration. Thick solid line: methyl cyclohexane, n=1.422, δ_(S)=16. Thin solid line: benzonitrile, n=1.528, δ_(S)=17.2; Dashed line: Chlorobenzene, n=1.524, δ_(S)=19.4.

FIG. 3( b) shows the corresponding simulated spectra calculated using a scalar wave approximation. The colloidal photonic crystal size was considered to be 11 (111) microsphere layers, accordingly to SEM analysis of the films. The position, width and intensity observed experimental were fitted having as the only variable parameter the (111) interplanar distance. By so doing, we can estimate the degree of swelling due to each solvent.

FIG. 4 shows the variation of the (111) interplanar distance versus the solubility parameter of different solvents, extracted from the fitting of the optical data for the composite silica crosslinked metallopolymer (PFS) gel colloidal photonic crystal film shown in FIG. 3. These results coincide qualitatively with previously reported studies of the swellability of the same type of pure bulk form of the metallopolymer gel performed by weight differential measurements.

FIG. 5 is a graphical representation showing the time response of the composite silica crosslinked metallopolymer (PFS) gel colloidal photonic crystal film, upon exposure to liquid carbon disulfide. The plot represents the absorbance at 843 nm plotted against time (0.1 second intervals), with this wavelength representing the maximum in intensity for the first stop band of the sample when swollen in carbon disulfide. Before starting the measurement, a background was taken of the dry sample to obtain a low initial absorbance value. As can be seen, the sample reaches its equilibrium swelling value within 0.2 to 0.4 seconds.

FIG. 6( a) shows a plot showing the spectra obtained for the same composite silica crosslinked metallopolymer (PFS) gel colloidal photonic crystal film sample with different degrees of oxidation after swelling the sample in carbon disulfide n=1.627, δ_(S)=20.5. The order of spectra, from least to most oxidized is: Solid squares; Empty squares; Empty circles; Solid circles; Empty diamonds. (b) The maximum values of the Bragg diffraction peaks shown in (a) plotted against the degree of polymer oxidation calculated from the intensity of the metallopolymer backbone ferrocenium ligand-to-metal-charge-transfer (LMCT) band maximum at 635 nm. The degree of oxidation of the metallopolymer is an estimate since it was calculated assuming a constant background level.

FIG. 7 shows a schematic of second-generation composite silica crosslinked metallopolymer (PFS) gel colloidal photonic crystal film sample fabrication. A colloidal crystal film grown by evaporative deposition of silica colloids is placed face down on a composite substrate made by sputtering a 75-300 nm film of copper onto a 0.1 mm thick PDMS film on a glass microslide. The assembly is heated to approximately 110° C. and a mixture of monomer and crosslinker are placed at the film edge, allowed to melt and imbibe the colloidal crystal film by capillary action. Alternatively, the monomer and crosslinker are allowed to melt on the copper coated substrate and the colloidal crystal film is pressed against the molten droplet, which infiltrates the colloidal crystal film. The composite substrate and colloidal crystal film are then bound together with binder clips, and thermally polymerized at 180° C. for 10-12 hours. The sample is then separated with a scalpel′ which breaks the copper-PDMS interface. The copper is then etched for 5 minutes in a iron trichloride/ammonium chloride/water bath.

FIG. 8 shows SEM images of second-generation composite silica crosslinked metallopolymer (PFS) gel colloidal photonic crystal film samples. a) Low-resolution image of film cross-section. b) High-resolution image of cross-section. Both white scale bars represent 1 micrometer. Note the absence of an overlay of the infiltrated PFS on the top surface of the colloidal crystal film.

FIG. 9 shows the optical response of a composite silica cross-linked metallopolymer (PFS) gel colloidal photonic crystal film sample, exposed to solvent vapour. Using a custom-built optical cell, optical properties of samples were probed while monitoring the vapour pressure of carbon disulfide used as a sample solvent. a) Optical spectra of the sample exposed to increasing pressure of solvent vapour, starting from the bottom plot. b) Optical spectra of the sample exposed to decreasing pressure of solvent vapour, starting from the bottom plot. c) Position of the stop-band of the sample vs. the vapour pressure of solvent for increasing and decreasing vapour pressure (indicated by black arrows), note the absence of hysteresis in the stop band wavelength as the solvent vapor pressure is changed.

FIG. 10 shows deswelling kinetics of a solvent vapour swollen composite silica crosslinked metallopolymer (PFS) gel colloidal photonic crystal film sample exposed to vacuum. Note the sub-second time response of the system.

FIG. 11 is a cyclic voltamagram (CV) of a film of metallopolymer (PFS) gel supported on a conductive ITO substrate. This CV was obtained using a scan rate of 100 mV/s in dichloromethane with 0.5 M of tetrabutylammonium hexafluorophosphate electrolyte.

FIG. 12 is a plot of the composite silica crosslinked metallopolymer (PFS) gel colloidal photonic crystal film stop band position (blue line) versus the electrochemical potential applied (bars). The electrolyte consists of 0.5 M tetrabutylammonium hexafluorophosphate in dichloromethane. For each step the potential was kept at the indicated value for 2 minutes before the stop band position was determined. Note the correlation between the stop band wavelength and applied potential of the composite silica crosslinked metallopolymer (PFS) gel colloidal photonic crystal film.

FIG. 13 is a plot of the intensity of the absorbance at 635 of a composite silica cross-linked metallopolymer (PFS) gel colloidal photonic crystal film sample, representing the ligand to metal transition of oxidized ferrocene (red line), versus the electrochemical potential applied (bars). The electrolyte consists of 0.5 M tetrabutylammonium hexafluorophosphate in dichloromethane. For each step the potential was kept at the indicated value for 2 minutes before the absorbance value was determined. Note the extremely good correlation between the applied potential and the degree of oxidation of the composite silica cross-linked metallopolymer (PFS) gel colloidal photonic crystal film.

FIG. 14 is an optical photograph of a pixel of planarized composite silica cross-linked metallopolymer (PFS) gel colloidal photonic crystal film supported on a F-doped tin oxide substrate. The photograph on the left shows the pixel in its reduced state and on the right its oxidized state. The colour change is due to the light yellow colour of reduced ferrocene and the blue colour of oxidized ferrocene. The stop band of this sample occurs in the near infrared, and thus is not visible in an optical picture.

FIG. 15 are scanning electron micrographs (SEM) of a free-standing film of macroporous metallopolymer (PFS) gel fabricated by sputtering a layer of gold on the top side of a composite silica crosslinked metallopolymer (PFS) gel colloidal photonic crystal film and subsequently etching the silica spheres and substrate with 1.5% aqueous HF. The scale bars in the main figure and the top left inset represent 1 micrometer, whereas the scale bar in the bottom right inset represents 10 micrometers. Note the high structural quality of the film sample, which clearly shows the existence in the metallopolymer gel matrix of well ordered macropores replicating the size and shape and location of the original fcc close packed microspheres in the colloidal crystal and well ordered mesopores reflecting the locations in the colloidal crystal where fcc close packed microspheres just touched.

FIG. 16 is a schematic diagram of the mode of operation of the polychrome composite colloidal photonic crystal metallopolymer gel described in this application. This material can uptake solvent in liquid or vapour form causing it to go from the left to middle in this illustration. This increases the lattice constant and red-shifts the optical Bragg diffraction wavelength. Oxidation of the material changes the properties of the material, causing it to shrink resulting in a blue-shift in optical Bragg diffraction wavelength as indicated on going from the middle to the right in this illustration. The illustration of the mode of operation of the material describes the behaviour of the material when exposed to a non-polar solvent, whereas in a sufficiently polar solvent the structure would be more swollen in the oxidized state and thus oxidation would red-shift the diffraction wavelength.

FIG. 17 shows a schematic of a tunable photonic crystal device in accordance with one aspect of the present disclosure.

FIGS. 18A-E show graphs of measurements from one example of a tunable photonic crystal device in accordance with one aspect of the present disclosure.

DETAILED DESCRIPTION OF INVENTION

As used herein, the term “metallopolymer” means a metal-containing molecule or molecular assembly having at least one type of chemical unit which repeats itself more than once, with metal atoms and/or groups of metal atoms chemically integrated into the backbone of the polymer but with the possibility that these metallopolymers could also contain metal atoms or groups of metal atoms chemically integrated into side arm functional groups of the metallopolymer or metallooligomer.

In this detailed description, we provide novel methods for electro-mechanically color tuning over a wide wavelength range, in a continuous and fine, rapid and reversible, reproducible and predictable manner, a synthetic composite material that is comprised of predetermined area and thickness film or patterned film or shape of any dimension or array of shapes of any dimension of a composite cross-linked metallopolymer network colloidal photonic crystal film or patterned film or shape of any dimension or array of shapes of any dimension whose polychrome optical functionality portends utility in such application areas as wavelength tunable optical telecommunication filter, mirror, multiplexor, compensator, limitor and switching as well as sensing, imaging, display and printing systems. The overall mode of operation of the widely wavelength tunable polychrome composite crosslinked metallopolymer (PFS) gel colloidal photonic crystal material described in this application is illustrated in FIG. 16. Specifically, FIG. 16 shows a schematic diagram of the mode of operation of the polychrome composite colloidal photonic crystal metallopolymer gel material described in this application. The material can uptake solvent in liquid or vapour form causing it to go from the left to middle in this illustration. This increases the lattice constant and red-shifts the optical Bragg diffraction wavelength. Oxidation of the material changes the properties of the material, causing it to shrink resulting in a blue-shift in optical Bragg diffraction wavelength as indicated on going from the middle to the right in this illustration. The illustration of the mode of operation of the material describes the behaviour of the material when exposed to a non-polar solvent, whereas in a sufficiently polar solvent the structure would be more swollen in the oxidized state and thus oxidation would red-shift the diffraction wavelength.

The present method of wavelength tuning a composite material involves producing an ordered array of microparticles having a selected refractive index embedded within a cross-linked metallopolymer network having a different refractive index, the ordered array of microparticles has a lattice spacing giving rise to Bragg reflection at a characteristic wavelength when the composite material is illuminated. The microparticles may include, but are not limited to, spheres, ellipsoids, rods, sphere containing polyhedra, cubes, and polyhedra, having cross-sectional dimensions from about 60 nanometers to about 100 micrometers. The microparticles may be made from, but not limited to, insulators, polymers, metals, and semiconductors. In one embodiment, the microparticles are monodisperse microspheres (3-5%) made of silica having diameters from about 60 nanometers to about 100 micrometers. As an alternative to solid particles, the ordered array may be formed by inverting the metallopolymer particle composite to dissolve out the particles leaving behind an array of voids in the metallopolymer, which may be filled with a suitable gas at a suitable pressure. Air has a refractive index of unity which will give a refractive index contrast with the metallopolymer making up the cross-linked polymer network.

It will be understood that when referring to “metallopolymers” the inventors also intend that the present invention may be comprise metallooligomers which have a smaller number of repeat units than typical of polymers. Therefore, as far as the present application is concerned the term “metallopolymers” also means “metallooligomers”.

The microparticles may be formed as a thin film on a substrate which may be a metal, insulators, semiconductors, semimetals, polymers and liquids. They may be grown on the substrate surface in a pattern to form a component of a circuit, optical or electronic, depending on the application or end use of the material. The constituents may also be formed as a free-standing monolith structure, or an array of structures, in other words in the case of microspheres, a large bulk crystal may be grown and then infiltrated with the precursor to the cross linked polymer network. The microparticles themselves may be made from, but not limited to, insulators, polymers, metals, and semiconductors. In one embodiment, the microparticles are monodisperse microspheres made of silica. Both the surface of the first constituent microparticles and the surface of the arbitrary supporting substrate can be pre-treated or post-treated to increase the adhesion of the surfaces to the cross-linked metallopolymer network, for instance by anchoring a cross-linking group on these surfaces.

The cross-linked polymer network is produced using a metallopolymer having a backbone which includes metal atoms chemically integrated into the polymer backbone which may be connected together directly or through linking units. The cross-linked metallopolymer r network has an electronic configuration dependant on the metal atoms and the metal atoms are switchable between more than one electronic configuration. The cross-linked metallopolymer network being expandable and contractible in response to controlled uptake and expulsion, respectively, of fluid by the cross-linked metallopolymer network so that when the cross-linked metallopolymer network takes up the fluid it expands which shifts the Bragg reflection wavelength to longer wavelengths and when the cross-linked metallopolymer network expels the selected fluid it contracts which shifts the Bragg reflection wavelength to shorter wavelengths. The amount of fluid uptake and expulsion is controlled by controlling the electronic configuration of the cross-linked p metallopolymer network.

The switching of the electronic configuration may include changing the charge distribution in the metal-containing cross-linked metallopolymer network, including polarizing electrons in the outer orbitals with respect to the nuclei thereby varying ion, dipole, induced dipole and fluctuating dipole interactions and the like. As well, the switching of the electronic configuration of the cross-linked metallopolymer network can be performed on a localized spatial area of the cross-linked metallopolymer network, for instance by fabricating the composite material on patterned electrodes.

In one embodiment of the metal containing cross-linked metallopolymer network the different electronic configurations refers to multiple oxidation states and the metal atoms are switchable between more than one oxidation state which changes the local environment thereby giving rise to the uptake or expulsion of fluid. Thus in this case the switching electronic configuration of the cross-linked metallopolymer network includes switching a given proportion of the metal atoms from one oxidation state into another state.

The cross-linked metallopolymer network may be produced containing metal atoms including but limited to titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, niobium, molybdenum, ruthenium, rhenium, platinum, palladium, rhodium, and zinc and combinations thereof. In one embodiment, the unit from which the material is made is a metal-containing bridged metallocenophanes containing some of the metals mentioned above, which may be iron with a silicon atom bridging the two cyclopentadienyl ligands in the case of strained sila-1-ferrocenophanes so that the cross-linked metallopolymer network is comprised of a polyferrocenylsilanes.

Sila-1-ferrocenophanes giving rise to linear metallopolymer are species including, but not limited to, dialkylsila-1-ferrocenophanes, alkylalkoxysila-1-ferrocenophanes, dialkoxysila-1-ferrocenophanes, cycloalkylsila-1-ferrocenophanes, diarylsila-1-ferrocenophanes, alkylaryisila-1-ferrocenophanes, alkylalkenylsila-1-ferrocenophanes, alkylalkynylsila-1-ferrocenophanes or combinations thereof. Sila-1-ferrocenophanes which give rise to a cross-link between polymer chains can include, but are not limited to, cyclobutylsila-1 ferrocenophane, sila-1,1′-diferrocenophane, 1,2-bis(methylsila-[1]-ferroc-enophane)acetylene, 1,4-bis(methylsila-[1]-ferrocenophane)benzene, bis(methylsila-[1]-ferrocenophane)-1,4-diethynylbenzene, and 1,2-bis(methylsila[1]-ferrocenophane)ethane or combinations thereof. These species may be polymerized thermally, or with a variety of polymerization initiators such as transition metal catalysts or carbanions or electromagnetic radiation of various wavelengths.

A cross-linked metallopolymer network may be formed using the above-mentioned metal containing monomers using a mixture of compounds including about 50-100 weight % monomer, 0-30 weight % crosslinlker, and 0-20 weight % initiator. The resulting network consists of cross-linked polyferrocenylsilane, with a density of crosslinks controllable by the proportion of crosslinker in the above mixture. The porosity of the metallopolymer network may be tuned if the above mixture is diluted in an inert substance, such as a solvent, which can be removed after polymerisation.

The oxidation state of the metal may be switched by one or more of several different methods, including but not limited to the application of a stimulus such as chemical redox reactions, photochemical redox reactions, thermochemical redox reactions and electrochemical redox reactions. A thermochemical redox reaction may be effected by using a compound which fragments into reactive compounds which may be oxidizing or reducing agents, such as the thermal cleavage of peroxides giving two oxidizing oxygen-centered radicals. A photochemical redox reaction may be effected by using a compound which fragments into reactive compounds which may be oxidizing or reducing agents, such as the photocleavage of chloroform which gives rise to an oxidizing chlorine radical.

The metal atoms chemically integrated into the polymer backbone are connected together directly or through linking units or combinations thereof. For example, the metal containing polymer backbone may have periodic segments in which two or more metal atoms are bonded directly together to impart a certain set of chemical, physical, electrochemical, and electronic properties to the cross-linked polymer network. Alternatively, each metal may be spaced from its nearest neighbour by means of a linking unit. The linking units are selected to impart pre-selected chemical, physical, electrochemical, and electronic properties to the cross-linked polymer network. The linking units may include, but are not limited to, substituted or unsubstituted carbanions, conjugated carbanions, linear olefins, cyclic olefins, acetylenes, phosphines, amines, carbonyls, carbenes, alkoxides or combinations thereof.

The metal atom units chemically integrated into the polymer backbone may bear side-chain ligands which may include, but are not limited to, substituted or unsubstituted carbanions, conjugated carbanions, linear olefins, cyclic olefins, acetylenes, phosphines, amines, carbonyls, carbenes, alkoxides or combinations thereof which themselves may be bonded to metal atom units of various types.

Depending on the method of synthesis and formulation of the metallopolymer, the cross-links in the polymer network may arise to due chemical bonds, physical bonds, nanoparticles, surfaces, hydrogen bonds, coordination bonds, electrostatic interactions, hydrophobic interactions, fluorophobic interactions and phase-separated domains or combinations thereof. The crosslinks in the metallopolymer network may be selected to be either electronically conducting or electronically insulating or mixtures thereof.

The wavelength tunable composite material may be produced by a) forming an ordered array of the first constituents, which displays Bragg reflection, in a cross-linked metallopolymer network precursor mixture, and then b) inducing cross-linking of the cross-linked metallopolymer network precursor mixture and converting it to a cross-linked metallopolymer network with a given number density of cross-links.

Step a) may include organizing the microparticles into an ordered array which displays Bragg reflection, and then infiltrating the cross-linked metallopolymer network precursor mixture into void spaces between the first constituents. Alternatively, step a) may include organizing the microparticles into an ordered array in the presence of the cross-linked metallopolymer network precursor mixture.

The metallopolymer network may be produced with a pre-selected number density and distribution of crosslinks throughout the composite material which can be controlled by known polymer processing conditions. For example, controlling the given number density of cross-links may be achieved by the controlled cleavage of a predetermined number of bonds in the cross-linked metallopolymer network. The controlled cleavage may be performed by electrochemically cycling between more than one predetermined electronic configurations (e.g. oxidation states) of the network.

The surface of the microparticles may be modified in a manner suitable to increase the adhesion between the first constituents and the cross-linked metallopolymer network as well as with a chosen substrate. For example, the surfaces of the microparticles may be functionalized with groups which enhance binding of the metallopolymer network to the surfaces of the microspheres as well as the surface of a chosen substrate.

The cross-linked metallopolymer network precursor mixture may be a liquid which is infiltrated into void spaces between the first constituents. Alternatively, the cross-linked metallopolymer network precursor mixture may be a solid which is heated and infiltrated into the void spaces between the first constituents as a liquid melt. The cross-linked metallopolymer network precursor mixture may be a solid which is infiltrated into the void spaces between the microparticles by sublimation. The cross-linked metallopolymer network precursor mixture may also be a solid which is infiltrated into the void spaces as a solution in a liquid. Or, the cross-linked metallopolymer network precursor mixture may be a liquid or a solid dissolved in solution and the metallopolymer network precursor mixture electrodeposited by using an oxidative potential or a reducing potential, where the application of the controlled potential causes a change in solubility in the metallopolymer network precursor mixture and results in a solid being deposited in the void spaces of the first constituents.

The composite may be produced in a manner which avoids the top surface of the array of the microparticles being overcoated by the cross-linked metallopolymer network precursor mixture by a thickness of more than the cross-sectional dimension of the first constituent particles. This can be done by pressing an elastomeric substrate against the array of first constituents infiltrated with the cross-linked metallopolymer network precursor mixture, squeezing out any excess which is not in the spaces between the first constituents themselves.

A controlled amount of polymerisation initiator may be incorporated into the cross-linked metallopolymer network precursor mixture and the cross-linking of the cross-linked metallopolymer network precursor mixture by a stimulus selected from time, change in temperature, electromagnetic radiation, chemical and electrochemical reaction.

The cross-linked metallopolymer network precursor mixture may include a pre-selected amount of an additive which is removed (for example by dissolving) after cross-linking resulting in a cross-linked metallopolymer network of pre-selected porosity. Conversely, additives may be incorporated into the cross-linked metallopolymer network following cross-linking. These can be chosen to modify the properties of the cross-linked metallopolymer network, and can include solvents, solutions, gases, solids, dyes, molecules, metal nanoclusters and semiconductor nanoclusters, macromolecules, molecule assemblies, as well as particles selected from the group of spheres, ellipsoids, rods, sphere containing polyhedra, cubes, and polyhedra, having cross-sectional dimensions from about 0.1 nanometers to about 1 micrometer, or combinations thereof.

The products, and methods used to produce these products in accordance with the present application will now be illustrated with the following non-limiting examples which are meant to be exemplary only.

EXAMPLE 1 Synthesis of Planarized Colloidal Photonic Crystal-Metallopolymer-G-el Network

To put the present method in perspective, the materials investigated in this study are planarized composite colloidal photonic crystals comprised of an ordered fcc arrangement of sub-micrometer disconnected microspheres in a matrix of weakly crosslinked poly(ferrocenylsilane) (PFS), a swellable redox-active metallopolymer gel, that is, metallopolymer gel, K. Kulbaba, M. J. MacLachlan, C. E. B. Evans, I. Manners, Macromol. Chem. Phys. 202, 1768 (2001).

This new class of metallopolymer-colloidal crystal composites with metal atoms integrated directly the backbone of the metallopolymer matrix overcome deficiencies in organic polymer analogues, like the class represented by but not limited to polyacrylamides, as well as introduce additional functionality by virtue of the metal-containing metallopolymer used.

Poly(ferrocenylsilane) (PFS), featured in this application, is a metallopolymer whose main chain is composed of alternating substituted silicon atoms and ferrocene groups connected at the 1- and 1′-positions of the cyclopentadiene (Cp) rings. Thermal ring-opening polymerization (ROP) of strained, ring-tilted [1]silaferrocenophanes affords high molecular weight polymer, D. A. Foucher, B. Z. Tang, I. Manners, J. Am. Chem. Soc. 114, 6246 (1992). The monomer used in this example was (ethylmethyl)sila-[1]-ferrocenophane, (K. Temple, J. A. Massey, Z. Chen, N. Vaidya, A. Berenbaum, M. D. Foster, I. Manners, J. Inorg. Organomet Poly. 9, 189 (1999)) bearing asymmetric substituents on the silicon atom, avoiding the possibility of micro-crystallization within the metallopolymer network. The crosslinker was sila(cyclobutyl)-[1]-ferrocen-ophane, constituted of two strained rings, which can both be ring-opened thermally (M. J. MacLachlan, A. J. Lough, I. Manners, Macromolecules 29, 8562 (1996)).

There are a wide variety of chemical modifications that can be performed on this metallopolymer system to tune its mechanical, redox and thus optical characteristics. For instance, the described crosslinker could be replaced by species giving rise to electrically conductive crosslinks. These include 1,2-bis(methylsila-[1]-ferrocenophane)acetylene-, 1,4-bis(methylsila-[1]ferrocenophane)benzene, bis(methylsila-[1]-ferroce-nophane)-1,4-diethynylbenzene, 1,2-bis(methylsila-[1]-ferrocenophane)ethen-e.

The synthesis and crystal structure of one completely new example of these is shown in FIG. 1A. More particularly, FIG. 1Aa shows the synthesis of a next generation cross-linker for the composite silica cross-linked metallopolymer (PFS) gel colloidal photonic crystal film. The cross-linker in the new PFS comprises two polymerizable silaferrocenyl rings appended to the two ends of an electrically conductive, pi-conjugated diethynylbenzene group. FIG. 1Ab) shows the single crystal x-ray structure determination of the product shown in the synthetic scheme. Note that the conductive cross-links in this next generation composite silica cross-linked metallopolymer (PFS) gel colloidal photonic crystal are designed to improve the swelling and shrinking time response to an electrochemical stimulus by increasing the rate of charge-transport within the film.

FIG. 1B shows a schematic of the steps involved in fabrication of the composite material and includes (i) evaporative deposition of silica colloids; (ii) 200° C., 12 hours, vacuum; (iii) treatment with capping agent 1; (iv) infiltration of monomers 2 and 3, removal of solvent at 300 mm Hg; (v) sample covered with PTFE sheet, glass slide and bound with binder clips; (vi) 190° C., 13 hours, N₂; and (vii) careful removal of clips, PTFE and glass cover.

To produce high quality colloidal photonic crystals, we start with highly monodisperse (standard deviation <2-3% of average sphere diameter) silica microspheres of 280.+−0.5 nm diameter (as measured by Scanning Electron Microscopy (SEM)) produced by the controlled hydrolysis of tetra(ethoxy)silane, (W. Stober, A. Fink, E. J. Bohn, J. Colloid Interface Sci. 26, 62 (1968)). The polydispersity was further narrowed by 2-3 fractionation steps, where the microspheres were allowed to settle slightly, and the bottom and top of the suspension were pipetted and discarded. Planar silica colloidal crystals were produced by the evaporative deposition method (P. Jiang, J. F. Bertone, K. S. Hwang, V. L. Colvin, Chem. Mater. 11, 2132 (1999)) on glass microscope slides, and the film on one side of the glass was wiped off.

Colloidal crystals could also be grown on electrically conductive substrates such as Indium-Tin Oxide (ITO) or Fluorine Tin Oxide (FTO) coated glass slides. For example, ITO-glass slides were cleaned by the standard RCA protocol (5:1:11H2O:NH3(aq):30% H2O2(aq), and then subjected to the evaporative deposition of silica microspheres as described above. One notable modification was the addition of 0.1 mL diisopropylethylamine to the 15 mL of ethanolic sol, without which no colloidal crystal film deposited on the ITO surface. These colloidal crystals were characterized by UV-Vis-NIR spectroscopy, then dehydrated and brought into a nitrogen-filled glove box. The surface of the microspheres and substrate was then modified with chlorosilane 1 in dry hexanes, where displacement of the chlorine by silica silanol groups produces a surface layer of polymerizable groups (D. L. Zechel, K. C. Hultszch, R. Rulkens, D. Balaishis, Y. Ni, J. K. Pudelski, A. J. Lough, I. Manners, D. A. Foucher, Organometallics 15, 1972 (1996)).

Alternatively, compound 1 can be replaced with crosslinker 2, which reacts with the surface silanol groups to form a surface tethered layer of polymerizable silacyclobutyl groups. This step is essential to obtain a colloidal crystal material with good adhesion to the substrate. A very concentrated solution of 10 wt % crosslinker 2 and 90 wt % monomer 3 in dry benzene was then dropped onto the colloidal crystal film, and the solvent was removed by drying in partial vacuum. The sample, a sheet of clean, polished poly(tetrafluoroethylene) (PTFE; Teflon®) and another glass slide are bound together with binder clips, and the sample thermally polymerized. Careful separation of the assembly yielded the desired silica-PFS composite colloidal crystal film, which was soaked in tetrahydrofuran (THF) overnight to remove any oligomers not polymerized into the PFS network.

A cross-sectional SEM image of one sample is shown in FIG. 2. This SEM image of a cross-section of the composite silica crosslinked metallopolymer (PFS) gel colloidal photonic crystal film shows the glass substrate, the infiltrated colloidal crystal, and the bulk metallopolymer (PFS) overlayer. The inset shows a magnified view of (111) crystal planes exposed during sample cleavage, confirming the face-centered cubic (fcc) arrangement of microspheres in these colloidal crystals.

Variants of this method have been used to improve, notably, the mechanical stability of the samples upon cycling. Upon infiltration and drying of the monomers as described above, the PTFE cover and glass slide are replaced by a glass slide sputter-coated with 6000 Angstroms of copper metal, the copper coating facing the colloidal crystal sample. The assembly is bound with binder clips, and the sample thermally polymerized at a nitrogen partial pressure of 100-150 Torr for 15 hours at 190° C. Following polymerization, the top glass cover can be easily separated, and the exposed copper coating etched in 10 minutes with an aqueous solution of _(FeCl3) and NH₄Cl.

As well, controlled amounts of PFS homopolymer (various alkyl groups on the backbone silicon atoms) can be incorporated into the film along with monomers during the infiltration step. The inclusion of polymer has two functions, the first being to aid in the infiltration step by conferring to the monomer/crosslinker solution enhanced viscosity and lowered tendency to crystallize, both resulting in more even and reproducible infiltration. As well, the washing step serving to remove unreacted oligomers will also remove the incorporated homopolymer, providing a readily tunable porosity. This allows one to tune optical properties through control of filling fraction, and kinetic response by increasing free volume in the polymer network.

EXAMPLE 2 Synthesis of Planarized Colloidal Photonic Crystal-Metallopolymer-G-el Network Without Polymer Overlayer, by Melt Infiltration

The method detailed here describes the fabrication of planarized composite colloidal photonic crystals consisting of an ordered fcc arrangement of sub-micrometer disconnected silica spheres in a matrix of weakly cross-linked PFS as per Example 1. In the previous example the material is produced with a polymer overlayer of variable thickness, whereas in this example the polymer overlayer is reproducibly less than a sphere diameter. A schematic of the procedure is shown in FIG. 7. This first step consists of cleaning a glass microslide by sonication in acetone followed by water. It is then placed on a silicon wafer, which has been cleaned in piranha (see previous example), water, then dried and exposed to perfluorooctyltrichlorosilane to make it non-adhesive. Glass microslips of 0.1 mm thickness are used as spacers between the glass slide and the silicon wafer. A liquid PDMS prepolymer is poured onto the assembly, the air removed by vacuum, and the whole is placed in a oven at 60° C. for 24 hours to cure the PDMS. The silicon wafer is lifted off, leaving the glass slides with a 0.1 mm thick film of PDMS, onto which is sputtered between 75 and 300 nm of copper metal.

Next, a colloidal crystal film as prepared by the method described in example 1 is treated with the crosslinker 2 in dichloromethane, using a 1-10 mol % of 4-dimethylamino-pyridine as catalyst. The film is then washed well in dichloromethane and dried. The copper coated composite substrate as describe above is then placed copper side up onto a hot plate in a nitrogen-filled glove box, with the hot plate set at a temperature of between 50 and 130° C. Approximately 50 mg of a solid mixture of monomer 1 and crosslinker 2, typically 10 weight % of 1 in 2, is then placed on the copper and allowed to melt. As soon as the mixture is molten, the prepared colloidal crystal film, which has also been allowed to equilibrate at the melting temperature, is pressed colloidal crystal side down against the copper. The assembly is quickly bound together with fold back binder clips, and polymerized under nitrogen at 180-200° C. for 10-20 hours.

After polymerization, the assembly is removed from the furnace, the clips removed, and a scalpel blade used to pry apart the colloidal crystal film and copper coated substrate. In this way, a planarized composite colloidal photonic crystals consisting of an ordered fcc arrangement of sub-micrometer disconnected silica spheres in a matrix of weakly crosslinked PFS is obtained, where the copper film originally on the PDMS has been transferred to the top of the planarized photonic crystal. The copper-coated film is then agitated in a solution of typically 0.2 g FeCl₃ and 3 g NH₄Cl in 150 mL distilled water for 5 minutes, which etches away the copper. A cross-sectional image of one of these samples is shown in FIGS. 8 a) and 8 b) in which FIG. 8 a) shows a low-resolution SEM image of the film cross-section and FIG. 8 b) shows a high-resolution SEM image of the film cross-section. Both white scale bars represent 1 micrometer. Note the absence of an overlay of the infiltrated PFS on the top surface of the colloidal crystal film. FIGS. 8 a) and 8 b) demonstrate that the film is fully filled with no excess polymer over-layer. The role of the PDMS in this process is to ensure conformal pressure against the sample surface, and provides greater tolerance to adventitious particulate matter.

EXAMPLE 3 Optical Properties of Liquid Solvent Tuneable Planarized Colloidal Photonic Crystal-Metallopolymer-Gel Network

Optical properties of both dry and solvent soaked samples were measured in a standard IR cell mounted with a rectangular quartz plate, PTFE spacer and a quartz plate with 2 drilled holes allowing for injection and removal of solvent, squeezed together by a metal frame with a window and tightening screws. A 0.3 mm aperture was affixed to the cell in order to obtain spectra of a small sample area. Spectra were collected using a UV-vis-NIR spectrometer (Perkin-Elmer Lambda 900 model), orienting the sample (111) surface perpendicular to the incident beam using alignment marks. A portion of the experimentally obtained spectra is shown in FIG. 3( a). The peak shown represents selective reflection of a narrow band of wavelengths due to optical Bragg diffraction from the (111) planes of the colloidal photonic crystal, and the secondary maxima on either side of the main peaks are due to interfering reflections from the top and bottom of the sample (Fabrey-Perot fringes).

In order to estimate the effect of the swelling on the structure of the colloidal photonic crystal, the results of the optical characterization were analyzed employing a theoretical model based on a scalar wave approximation (K. W.-K. Shung, Y. C. Tsai, Phys. Rev. B 48, 11265 (1993)). This simple model has been proven to be valid to describe the transmittance and reflectance of finite size photonic crystals at the spectral region corresponding to that of lower energy photonic bands such as the ones we investigate here (I. Tarhan, G. H. Watson, Phys. Rev. B 54, 7593 (1996), J. F. Bertone, P. Jiang, K. S. Hwang, D. M. Mittleman, V. L. Colvin, Phys. Rev. Lett. 83,300 (1999), H. Miguez, S.-M. Yang, G. A. Ozin, Appl. Phys. Lett., 81, 2493-95 (2002), and Y. A. Vlasov, M. Deutsch, D. J. Norris, Appl. Phys. Lett. 76, 1627 (2000)).

In the present case, knowing the refractive index of both the silica microspheres and the infiltrated cross-linked polymer, n=1.425 and n=1.65 respectively (F. Garcia-Santamaria, H. Miguez, M. Ibisate, F. Meseguer, C. Lopez, Langmuir 18, 1942 (2002), and J. Galloro, M. Ginzburn, H. Miguez, S. M. Yang, N. Coombs, A. Safa-Sefat, J. E. Greedan, I. Manners, G. A. Ozin, Adv. Funct. Mater. 2002, 12, 382) as well as that of the solvent, we are able to obtain the increase of the (111) interplanar distance d(111) resulting from the swelling process. We take into account the variation of the refractive index of the colloidal photonic crystal interstitial sites due to incorporation of the solvent into the polymer network when the swelling occurs.

We also include the presence of a substrate (glass slide) and a superstrate (polymer excess, see FIG. 2) of different refractive index (D. M. Mittleman, J. F. Bertone, P. Jiang, K. S. Hwang, V. L. Colvin, J. Chem. Phys. 111, 345 (1999).). By using this approach, we fit the simulated reflectance spectra to the experimental ones considering d(111) as the only adjustable parameter. At the same time, we reproduce the particular optical features observed for each one of the solvents, such as reflectance peak width, position and intensity. FIGS. 3 a and 3 b summarizes the main results of the fitting. FIGS. 3 a and 3 b show, respectively, experimental and theoretical results for the starting dry polymer-silica colloidal crystal composite, and the same film while soaked in various solvents. More particularly, FIG. 3( a) shows experimental transmission spectra of the same silica-cross linked gel colloidal photonic crystal soaked with solvents of different solubility parameter and refractive index. Circles: sample prior to solvent infiltration. Thick solid line: methyl cyclohexane, n=1.422, δ_(S)=16. Thin solid line: benzonitrile, n=1.528, δ_(S)=17.2; Dashed line: Chlorobenzene, n=1.524, δ_(S)=19.4. FIG. 3( b) shows the corresponding simulated spectra calculated using a scalar wave approximation. The colloidal photonic crystal size was considered to be 11 (111) microsphere layers, accordingly to SEM analysis of the films. The position, width and intensity observed experimental were fitted having as the only variable parameter the (111) interplanar distance. By so doing, we can estimate the degree of swelling due to each solvent.

Both the model and the experiment show explicitly how it is possible, by choosing the appropriate pair of solvents, to modulate the width of the photonic stop band keeping the spectral position of the maximum constant (results not shown). This is a consequence of the double character of the tuning process. On one side, the distance between microspheres increases during the swelling, which enlarges the lattice constant and simultaneously decreases the filling fraction of the silica microspheres in the structure. On the other hand, the refractive index contrast between microspheres and background is modified as a result of the incorporation of the solvent into the polymer network. The values of d(111) attained from this simulation are plotted versus the solubility parameter δ of the solvents in FIG. 4. Specifically, FIG. 4 shows the variation of the (111) interplanar distance versus the solubility parameter of different solvents, extracted from the fitting of the optical data for the composite silica cross-linked metallopolymer (PFS) gel colloidal photonic crystal film shown in FIG. 3. These results coincide qualitatively with previously reported studies of the swellability of the same type of pure bulk form of the metallopolymer gel performed by weight differential measurements.

The solubility parameter is a numerical value empirically describing the behavior of a specific solvent (J. H. Hildebrand, R. L. Scott, “The Solubility of Non-Electrolytes”, 3rd ed. Rienhold Publishing Corporation New York (1950); Dover Publications Inc. New York (1964)). It can be seen that a precise tuning of the intermicrosphere distance is achieved. It is worth mentioning that similar curves, although with much less resolution, have been obtain using the weight-difference technique (K. Kulbaba, M. J. MacLachlan, C. E. B. Evans, I. Manners, Macromol. Chem. Phys. 202, 1768 (2001)), these results being in good agreement with those herein presented.

A cross-linked polymer network cannot dissolve in any solvent, because the presence of crosslinks creates a “supermolecule” of effectively infinite molecular weight. Such a structure can absorb solvent, in order to maximize thermodynamically favorable contacts, but as the chains between crosslink points stretch out they pay an entropic price given a decrease in available degrees of freedom (P. J. Flory, “Principles of Polymer Chemistry”, Cornell Univ. Press, New York (1953)). Therefore, the degree of swelling of a polymer gel can depend on a variety of factors influencing solvent-polymer interactions (S. H. Gehrke, Adv. Polym. Sci. 110, 81 (1993)), making these systems inherently tunable. In the material we are studying, the greater the value of d(111), the more favorable is the solvent-polymer interaction permitting the determination of the polymer solubility parameter on this basis.

Swelling in these samples is not limited to solvents in the liquid phase. Solvent vapors as described in this application could also effect the said lattice dimension changes, with a potentially much faster response given the higher mobility of solvent molecules and the elimination of liquid-solid or liquid-gas interfaces which could limit response speed.

EXAMPLE 4 Temporal Optical Response to Liquid Solvent of Planarized Colloidal Photonic Crystal-Metallopolymer-Gel Network

A kinetics experiment was conducted to evaluate the response speed of the polymer-silica colloidal photonic crystal composite material upon exposure to solvent, with the results of the experiment shown in FIG. 5. FIG. 5 shows a graphical representation showing the time response of the composite silica crosslinked metallopolymer (PFS) gel colloidal photonic crystal film, upon exposure to liquid carbon disulfide. The plot represents the absorbance at 843 nm plotted against time (0.1 second intervals), with this wavelength representing the maximum in intensity for the first stop band of the sample when swollen in carbon disulfide. Before starting the measurement, a background was taken of the dry sample to obtain a low initial absorbance value. As can be seen, the sample reaches its equilibrium swelling value within 0.2 to 0.4 seconds.

In order to determine when the sample had reached its fully swollen state, the maximum in intensity of the first Bragg peak of the swollen sample was first noted. This wavelength was then monitored with respect to time, and carbon disulfide was injected into the cell. Before injecting the solvent, the absorbance value was low since a background had been taken of the dry sample, and this value was constant from 0 to 7 seconds.

We see then a brief increase, which is due to scattering by the air-liquid interface created by the solvent rising in the sample cell and crossing the incident beam. Next, we see a sharp drop in absorbance due to a decrease in refractive index contrast between the fluid content of the cell (solvent instead of air) and the quartz plates (nquartz/nair=1.54; ncarbon disulfide/nquartz=1.06), as well as with the glass substrate (Δnold=1.45; Δnnew=1.12) and PFS superstrate (Δnold=1.65; Δnnew=1.01). This decreases the light reflected at these interfaces and results in more light reaching the detector. After this decrease in intensity we see a rapid increase representing the swelling event, after which the sample attains a constant steady state absorbance value. The whole process, from initial injection of solvent onto the dry polymer-silica colloidal photonic crystal sample to the completely swollen state, occurs in 0.2-0.4 seconds.

EXAMPLE 5 Optical Properties of Solvent Vapor Tuneable Planarized Colloidal Photonic Crystal-Metallopolymer-Gel Network

To evaluate the response of planarized colloidal photonic crystal-metallopolymer-gel network samples to solvent vapor, a specialized optical cell was constructed. The sample holder consisted of an optical cuvette measuring 5 cm×10 cm×20 cm with an open top. The top of the optical cuvette was sealed against a main chamber fitted with a pressure gauge. From the chamber extended two glass tubes both fitted with two glass stopcocks, leaving a small volume of glass tubing, which could be filled with solvent vapor or evacuated under vacuum. The setup allowed for solvent vapor to be gradually or quickly introduced into the sample cell, and for vacuum to be applied in small increments or all at once.

Carbon disulfide was chosen as a test solvent to demonstrate the vapor swelling behaviour of the samples. Small amounts of solvent were iteratively loaded into the side chambers of the apparatus, and this side chamber open to the main chamber, which was under static vacuum. The optical spectra at a direction perpendicular to the substrate normal were monitored upon each cycle of increasing solvent vapour pressure. The results for the vapor swelling tests, are shown in FIG. 9 a which shows the optical spectra of the sample exposed to increasing pressure of solvent vapour, starting from the bottom plot. Conversely, to monitor the deswelling of the samples the side chamber could be placed under vacuum and this evacuated space equilibrated with the main chamber by opening the stopcock separating them, allowing the slow lowering of the pressure in the main chamber. The results of the deswelling experiment are shown in FIG. 9 b) which shows the optical spectra of the sample exposed to decreasing pressure of solvent vapour, starting from the bottom plot.

The full result of the experiment is shown in FIG. 9 c, where the peak wavelength of the stop-band of the sample is plotted against the solvent vapour pressure in the main chamber. FIG. 9 c shows the position of the stop-band of the sample vs. the vapour pressure of solvent for increasing and decreasing vapour pressure (indicated by black arrows), note the absence of hysteresis in the stop band wavelength as the solvent vapor pressure is changed. There seems to be very little hysteresis in the peak-pressure plot, indicating a well-controlled reversible process. As well as small iterative fillings, the sample could be fully swollen in a single step by loading the side chamber with a large concentration of solvent vapour. Full deswelling could be achieved by opening the main chamber to dynamic vacuum.

EXAMPLE 6 Temporal Optical Response to Solvent Vapour of Planarized Colloidal Photonic Crystal-Metallopolymer-Gel Network

To further investigate the speed and degree of switching of the planarized colloidal photonic crystal-metallopolymer-gel network to vapors, kinetic studies were undertaken using a CCD array fiber-optic spectrometer capable of capturing an entire spectrum in 0.1 seconds. After fully swelling the sample in solvent vapor, dynamic vacuum was applied and the optical properties monitored in situ. The result of the kinetics experiment is shown in FIG. 10, which show the deswelling kinetics of a solvent vapour swollen composite silica cross-linked metallopolymer (PFS) gel colloidal photonic crystal film sample exposed to vacuum. Note the sub-second time response of the system. It can be seen From FIG. 10 that the sample goes from the fully swollen to fully deswollen state in 0.5 seconds. The peak shift rate is thus in this example on the order of 200 nm/sec.

EXAMPLE 7 Optical Properties of Chemically Redox Tuneable Planarized Colloidal Photonic Crystal-Metallopolymer-Gel Network

PFS is composed of a backbone of redox-active ferrocene groups, and consequently the polymer itself is redox-active. Charges on the iron atoms are delocalized over the polymer chain via the Cp π-clouds and silicon electronic orbitals (R. Rulkens, A. J. Lough, I. Manners, S. R. Lovelace, C. Grant, W. E. Geiger, J. Am. Chem. Soc. 118, 12683 (1996)), and it therefore behaves as a polycation whose charge density can be controlled between a 0 and +1 charge for each polymer repeat unit (on average). Therefore, PFS would have continuously variable interactions with any solvent it is in contact with. As an experimental demonstration of this phenomenon, the PFS-silica composite opals were subjected to multiple partial oxidations using a solution in dichloromethane (DCM) of tris(4-bromophenyl)ammonium hexa-fluorophosphate, a one-electron oxidant, which is known to cleanly oxidize ferrocene derivatives (E. Steckhan, Angew. Chem., Int. Ed. Engl. 25, 683, (1986)). After thorough washing and drying, the oxidized sample was swollen in carbon disulfide and an absorbance spectrum taken. From this spectrum, the degree of polymer oxidation could be estimated based on the intensity of the characteristic ferrocenium LMCT band. After drying the sample, it was again oxidized, and these steps repeated until the LMCT transition no longer increased in intensity. The spectra obtained are shown in FIG. 6(A), and the wavelength at maximum intensity for the peaks is plotted against the degree of polymer oxidation in FIG. 6(B). Specifically, FIG. 6( a) is a plot showing the spectra obtained for the same composite silica cross-linked metallopolymer (PFS) gel colloidal photonic crystal film sample with different degrees of oxidation after swelling the sample in carbon disulfide n=1.627, δ_(S)=20.5. The order of spectra, from least to most oxidized is: Solid squares; Empty squares; Empty circles; Solid circles; Empty diamonds. FIG. 6( b) shows the maximum values of the Bragg diffraction peaks shown in (a) plotted against the degree of polymer oxidation calculated from the intensity of the metallopolymer backbone ferrocenium ligand-to-metal-charge-transfer (LMCT) band maximum at 635 nm. The degree of oxidation of the metallopolymer is an estimate since it was calculated assuming a constant background level.

As can clearly be seen, the diffracted wavelength in the swollen state steadily decreases with an increase in oxidation state, since a charged polymer cannot be effectively solvated by a non-polar solvent. Not only can the diffracted wavelength in this system be varied between two extremes, but all intermediate states can be individually and controllably accessed. An interesting point to note is the increase in peak position on going from the 90% to 100% oxidized sample. It could be that along with an increase in charge density, oxidation might also be changing the refractive index of the polymer either through anion incorporation or a polarizability change in the polymer itself.

When a sample was oxidized in the above fashion then reduced with a solution of decamethylferrocene in DCM, the spectrum obtained upon solvent swelling was virtually superimposable to the spectrum in the same solvent before oxidation (data not shown; see supporting information). This indicates that the system is reversible, a necessary requirement for use in practical applications of electro-photonically tuneable colloidal photonic crystals.

EXAMPLE 8 Optical Properties of Electrochemically Tuneable Planarized Colloidal Photonic Crystal-Metallopolymer-Gel Network

To test the behavior of planarized colloidal photonic crystal-metallopolymer-gel network samples when cycled electrochemically an electrochemical cell was constructed. The cell itself consisted of the optical cell used for probing the response of samples to liquid solvent as per example 6, and thin wires were sandwiched between the Teflon gaskets separating the top and bottom quartz plates delimiting the optical cell. The working electrode in the cell consisted of the planarized colloidal photonic crystal-metallopolymer-gel network supported on a conductive glass substrate such as ITO or FTO, and the conductive glass was contacted to a platinum wire fed outside the cell by a piece of Teflon sandwiching the two together. The counter electrode consisted of a platinum wire mesh with a platinum wire lead fed outside the cell. The reference electrode, properly a quasi-reference electrode, consisted of a silver wire where the end immersed in the electrochemical cell electrolyte had been previously coated with a layer of silver chloride by electrochemically anodizing the silver wire in 1 M aqueous HCl. Finally, the cell was then filled with dry solvent and supporting electrolyte in a nitrogen-filled glovebox and brought out of the glovebox for electrochemical and optical measurements. To first determine the electrochemical behavior of the metallopolymer itself, cyclic voltammetry was performed on the pure samples.

A sample cyclic voltammogram is shown in FIG. 11, where we can clearly see two oxidation and two reduction waves, where the first wave corresponds to oxidation/reduction of every other iron atom in the ferrocene units comprising the backbone of the metallopolymer. In this case an electrolyte consisting of 0.5 M tetrabutylammonium hexafluorophosphate in dichloromethane was used. If a sample was oxidized using a potential within the range of the two oxidation waves in the cyclic voltammogram, it was found to be quite stable to cycling. However, if a sample was oxidized beyond the second oxidation wave, some polymer chain degradation was observed, and further allowing the overoxidation to proceed resulted in the total degradation of the sample.

Once the redox potentials of the metallopolymer film were elucidated with cyclic voltammetry, an experiment was carried out to probe the stop-band position of the sample with respect to the degree of electrochemical oxidation. This was done, by monitoring the optical properties of the film using a CCD array fiber optics spectrometer. The incoming beam was oriented perpendicular to the sample surface. Shown in FIG. 12 are the results of one of these experiments which shows a plot of the composite silica crosslinked metallopolymer (PFS) gel colloidal photonic crystal film stop band position (blue line) versus the electrochemical potential applied (bars). The electrolyte consists of 0.5 M tetrabutylammonium hexafluorophosphate in dichloromethane. For each step the potential was kept at the indicated value for 2 minutes before the stop band position was determined. Note the correlation between the stop band wavelength and applied potential of the composite silica crosslinked metallopolymer (PFS) gel colloidal photonic crystal film. As can be seen, the more oxidizing is the potential applied to the sample, the greater the swelling of the sample and thus the greater the red-shift in the stop-band. This is presumably because of electroosmotic influx of the solvent molecules, which are solvating the counter-ions which diffuse into the film to ion-pair with the oxidize ferrocene moieties in the backbone of the polymer. As well as probing the stop-band position, we could also at the same time monitor the state of oxidation of the polymer indicated by the intensity of the ligand-to-metal-charge-transfer (LMCT) absorption of oxidized ferrocene moieties in the backbone of the polymer.

FIG. 13 shows a plot of the intensity of the absorbance at 635 of a composite silica cross-linked metallopolymer (PFS) gel colloidal photonic crystal film sample, representing the ligand to metal transition of oxidized ferrocene (red line), versus the electrochemical potential applied (bars). The electrolyte consists of 0.5 M tetrabutylammonium hexafluorophosphate in dichloromethane. For each step the potential was kept at the indicated value for 2 minutes before the absorbance value was determined. Note the extremely good correlation between the applied potential and the degree of oxidation of the composite silica cross-linked metallopolymer (PFS) gel colloidal photonic crystal film. As can be seen in FIG. 13, the redox state of the polymer is very well behaved, and can be tuned to any percent of oxidation simply by varying the applied potential, a unique property of this unique class of metallopolymer.

The effects of over-oxidation could be used to advantageously modify the swelling properties of planarized silica PFS-gel composite colloidal photonic crystals. It was found that if the samples were oxidized using a potential above the second oxidation wave of PFS then reduced again electrochemically, this resulted in a minor amount of chain cleavage, which effectively reduced the crosslink density of the gel and allowed the sample to swell to a greater degree than it did before the electrochemical over-oxidation.

In addition, the electrochemical tuning of the properties of the metallopolymer composite samples could be localized to a small area by pixellating a preformed sample. The pixellation was performed by micro-cutting with a tungsten carbide tip, which scratched through the conductive glass coating and effectively electrically isolated that area of the film. FIG. 14 shows two optical photographs of a pixel of planarized composite silica cross-linked metallopolymer (PFS) gel colloidal photonic crystal film supported on a F-doped tin oxide substrate. The photograph on the left shows the pixel in its reduced state and on the right its oxidized state. The colour change is due to the light yellow colour of reduced ferrocene and the blue colour of oxidized ferrocene. The stop band of this sample occurs in the near infrared, and thus is not visible in an optical picture so that the colors visible in this picture do not arise from diffraction, but rather arise from the color difference between the reduced and oxidized state of the polymer.

EXAMPLE 9 Removal of Microspheres from a Planarized Colloidal Photonic Crystal-Metallopolymer-Gel Network to Give a Macroporous Metallopolymer Film

The first step in the formation of a macroporous planarized colloidal photonic crystal-metallopolymer-gel network is the synthesis of a sample according to example 1 or example 2. Immersing these samples in a 1.5% solution of hydrofluoric acid in water for 2 days results in the removal of the silica microspheres and the formation of a free-standing macroporous PFS film.

To achieve a greater mechanical stability as well as confer an electrical contact to the redox-active macroporous metallopolymer film, a film of gold or other metal of a thickness between 10 and 2000 nm is deposited by argon-ion sputtering onto the top surface of a sample prepared according to example 1 or 2 prior to etching of the silica spheres. The silica is then etched as per above, and the result is a thin metal-coated film of inverse opal metallopolymer gel. SEM images of one of these films are shown in FIG. 15, clearly showing the absence of the silica spheres and substrate and the resulting three-dimensional porosity. More particularly, the scanning electron micrographs in FIG. 15 of a free-standing film of macroporous metallopolymer (PFS) gel fabricated by sputtering a layer of gold on the top side of a composite silica cross-linked metallopolymer (PFS) gel colloidal photonic crystal film and subsequently etching the silica spheres and substrate with 1.5% aqueous HF. The scale bars in the main figure and the top left inset represent 1 micrometer, whereas the scale bar in the bottom right inset represents 10 micrometers. Note the high structural quality of the film sample, which clearly shows the existence in the metallopolymer gel matrix of well ordered macropores replicating the size and shape and location of the original fcc close packed microspheres in the colloidal crystal and well ordered mesopores reflecting the locations in the colloidal crystal where fcc close packed microspheres just touched.

An optical microscope image of one of these free-standing films of macroporous metallopolymer (PFS) gel created by HF etching of a silica-PFS gel composite colloidal crystal is (not shown), shows the brilliant iridescent colors available from these materials and attests to their high quality structural properties and high level of optical photonic crystal properties.

To support the PFS-gel inverse opal film on a transparent polymethylmethacrylate substrate requires a slightly modified synthetic procedure. A colloidal crystal film as prepared by the method described in example 1 is treated with the crosslinker 2 in dichloromethane, using a 1-10 mol % of 4-dimethylaminopyridine as catalyst. The film is then washed well in dichloromethane and dried. The colloidal crystal film is then placed face up on the surface of a hot plate equilibrated at approximately 60° C., and onto the surface of the film is dropped about 50 mg of a mixture of di_(n)propylsila-1-ferrocenophane, 90% by weight, and silacyclobutylsila-1-ferrocenophane, 10% by weight. Once the monomer mixture has melted, a sheet of polymethylmethacrylate (PMMA, Plexiglass®) is placed on top of the molten droplet and the assembly clamped together with foldback binder clips. The sample is then thermally polymerized at 70° C. for 48 hours. Finally, the sample is soaked in a 1.5% aqueous HF solution for 1 to 4 days, which dissolves both the silica substrate and silica spheres and leaves a macroporous polymer inverse opal film on the PMMA substrate. Alternatively, the PMMA sheet can be replaced by a sheet of Mylar (polyethyleneterepthalate), a flexible transparent polymer.

What has been described is a composite photonic crystal material produced made of an metallopolymer gel film and microparticles located therein which has an adjustable lattice dimension so that the wavelength of optically Bragg diffracted light from the composite film can be tuned. The materials can be produced in the form of a film or patterned film or shape of any dimension or array of shapes of any dimension. These new materials have a continuously and finely, rapidly and reversibly, reproducibly and predictably, adjustable photonic crystal lattice dimension and concomitantly the predetermined ability to cause light of widely different wavelengths to be continuously and finely, rapidly and reversibly, reproducibly and predictably, and efficiently reflected or transmitted across the ultraviolet, visible and near infrared regions of the electromagnetic spectrum.

The tunable polychromicity of this composite colloidal photonic crystal material has utility in a myriad of applications requiring wavelength tunability of light, exemplified but not limited to optical components like filters, mirrors, multiplexors, compensators, limitors and switches of use in optical telecommunication systems as well as color tunable materials of use in imaging, display, printing, fingerprinting and sensing systems.

As mentioned in the Background above, it is noted that in the prior PCCA work a matrix encapsulates the colloidal crystal which is an organic polymer gel, which as amplified upon below is quite distinct in its composition and properties to the metallopolymer gels used in the photonic crystal-gel material described herein. In this context it is important to note that there exists a major distinction between the class of polymerized crystalline colloidal crystal arrays PCCAs that form the basis of all of Asher and co-workers studies and those that form the centerpiece of the embodiment described herein. In the approach of Asher and co-workers as well as other groups that followed his lead as mentioned above they exclusively self-assemble highly charged monodisperse spheres within an organic polymer hydrogel and immobilizes them within the organic polymer hydrogel as a non-close-packed colloidal crystal arrangement.

It is important to realize that this type of non-close-packed PCCA is not an ideal arrangement for the applications envisioned for this type of material first because it is very difficult to prepare the materials in a reproducible fashion and further because the structural and hence the optical properties of the materials are extremely sensitive to any adventitious changes in its immediate environment, like fluctuations of temperature, vibrations, humidity and so forth.

In sharp contradistinction to the PCCA, the colloidal photonic crystal materials that are the foundation of the work described in the present embodiment are intentionally designed to be different in a number of profound ways to the PCCAs of Asher and co-workers and furthermore at the same time avoid problems inherent in the PCCA materials employed in the work of Asher and co-workers. First the microspheres that constitute the desired colloidal photonic crystal used in the work described herein are pre-assembled into a stable and close packed arrangement. Second the polymer precursor is infiltrated into and polymerized within the void spaces between the constituent spheres that are intentionally close packed in the colloidal photonic crystal to provide a stable arrangement. Third the polymer that occupies the void spaces between the spheres in the colloidal photonic crystal is not an organic polymer gel and neither is it a polymer hydrogel instead it is a unique kind of metallopolymer gel with unique properties as a consequence of the fact that there exist metal atoms integrated into the backbone of the metallopolymer (or metallooligomer). Fourth, it is important to note that at the time that Asher and co-workers described most of his work on PCCAs, the metallopolymer (or metallooligomer) gel that is used exclusively in the work described herein had never before been synthesized and had never before been described in the open or patent literature.

Tunable Photonic Crystal Device

One application of the photonic crystal-gel composite material is its use in electronic displays. A robust electrically tunable photonic crystal device useable for such a display can be achieved by incorporating a planarized colloidal photonic crystal-gel polymer network into a sealed thin-layer electrochemical cell to form a tunable photonic crystal device.

A schematic diagram of the device is shown in FIG. 17. The device 50 comprises a film of the photonic crystal-metallopolymer-gel network 52 supported on a working electrode 54, and a counter electrode 56 spaced from the working electrode 54. The electrodes 54, 56 may be spaced apart by a spacer (not shown). The space between the two electrodes is filled with a conductive solution 58 and the device 50 is sealed. In the embodiment shown, the working electrode 54 is mounted on a substrate 60, and the counter electrode 56 is also mounted on a substrate 62.

In this form, the reflected wavelength of the device 50 may be tuned by changing the swelling of the polymer gel and hence the lattice spacing of the film 52, as described previously. By applying an electrical potential across the working electrode 54 and the counter electrode 56, ions and solvent from the conductive solution 58 may be made to flow in or out of the film 52, hence tuning the response of the film 52.

The completed device 50 may be connected to an electrical source, such as a potentiostat, to control the electrically tunable photonic crystal device 50. In this embodiment, the device 50 may be tuned by applying an electrical potential across the working and counter electrodes 54, 56. When an oxidative potential is applied to the device 50, electrons are drawn out of the polymer of the film 52, for example metal atoms in a metallopolymer gel, while anions from the conductive solution 58, surrounded by a solvent shell, are driven into the polymer in the film 52 to neutralize its positive charge build-up. The influx of both ions and solvent into the polymer causes it to swell and push apart the layers of microparticles, for example microspheres, in the film 52, resulting in a red-shift of the reflected optical diffraction peak. Applying a reducing potential runs the device 50 in reverse, with electrons docking onto the metallopolymer gel of the film 52 and the anions being expelled into the conductive solution 58. This causes the polymer in the film 52 to shrink, decreasing the spacing between the microspheres in the film 52, thus resulting in a blue-shift.

Typically, the film 52 may comprise a photonic-crystal gel composite material. The material may comprise microparticles or microspheres as described in the previous sections and examples. The material may also comprise a metallopolymer as described in the previous sections and examples or a conductive polymer as described below. The film 52 may be manufactured using the methods described above, or any common method known to those skilled in the art for manufacturing photonic crystal films.

The film 52 may comprise a conductive polymer. In one embodiment, the polymer in the film 52 is electroactive, that is, the polymer has atoms or chemical groups on the polymer—either on the polymer backbone itself, as a chain hanging off the backbone, or mixed with the polymer but not bound to the polymer—which respond to an electrical field or current. In some embodiments, these would be groups which can be oxidized or reduced, such as iron atoms or thiophene groups as found in common commercial conducting polymers, so that the polymer can maintain an electrical charge even after the electric current is removed. In other embodiments, the polymer includes groups which respond to the electric field, but do not oxidize or reduce. Such groups include ionic groups which would move within the electric field, but tend to drift back to their original positions once the field is removed.

In one embodiment, the photonic crystal-gel film 52 comprises a metallopolymer as the conductive polymer, such as a crosslinked network of polyferrocenylsilane (PFS). In other embodiments, the film 52 may comprise any of the materials described previously. The film 52 may comprise microspheres that form the photonic crystal, and the microspheres may comprise any of the materials described previously. In some embodiments, the film 52 does not include any microspheres, but contains an ordered array of voids.

In one embodiment, the conductive polymer may be: polypyrrole, polythiophenes (e.g., polyethylenedioxythiophene complex with polystyrenesulfonate), polyaniline, or polypyrrole and polythiophene electrodeposited into the photonic crystal. Some experiments have found that these conductive polymers produced less responsive devices.

The reflectance wavelength of the device 50 is not limited to the visible spectrum, and the device 50 is equally tunable in ultraviolet (UV) and infrared (IR) ranges. The tunable range of the device 50 may cover any range from IR to UV. In some applications, the device 50 may have a tunable range that covers the visible spectrum and IR, and the device 50 may be mounted on a black background, such that the device 50 may be tuned in the visible spectrum to provide a full range of color, and may be tuned to the IR spectrum to display black.

Note that although the film 52 is described as resting on the working electrode 54 and spaced from the counter electrode 56, it is equally possible for the film 52 to be resting on the counter electrode 56 and spaced from the working electrode 54. In some embodiments, the film 52 is free-floating between the electrodes 54, 56, and receives electrical current not directly from the working electrode 54, but via charge transfer through the conductive solution 58.

Possible materials for the electrodes 54, 56 are: conductive oxides, conductive ceramics, and carbon electrodes (e.g., graphite, amorphous carbon, or carbon nanotubes). Any other conductive material suitable for use as electrodes in an electrochemical cell may also be used. Although the electrodes 54, 56 have been described as being the same material, the electrodes 54, 56 may also be different materials.

Possible materials for the substrates 60, 62 comprise any of the substrate materials described previously for a photonic crystal-gel composite material. Typically, the substrates 60, 62 are selected to bind well with their respective electrodes 54, 56. In some embodiments, the electrodes 54, 56 may be formed directly on their respective substrates 60, 62 during manufacturing.

The electrodes 54, 56 have been described as being mounted on respective substrates 60, 62 for robustness. The use of substrates 60, 62 may also aid in the manufacturing of the cell 50. However, in embodiments where the electrodes 54, 56 are made of stiffer materials or are thicker in construction, it may not be necessary to use substrates 60, 62. This may improve the flexibility of the finished cell 50.

The electrodes 54, 56 may be spaced apart by a spacer. Possible materials for the spacer include thermoplastic polymer films, plastic films with adhesives, adhesives or epoxies deposited with a controlled thickness, or spacer beads which define the thickness of the cell 50 mixed into an adhesive or an epoxy.

The conductive solution 58 may comprise any suitable free conductive ions, ionic groups, or other charged particles. The conductive solution 58 may comprise any suitable solvent.

The entire device 50, and possibly including the electrical source, may range from quite small (e.g., 0.25 cm×0.25 cm or smaller) to quite large (e.g., enough for a display on the side of a building). The electrodes 54, 56 can similarly range from quite small to quite large, and may be as small as 1 micrometer. The spacer, if used, may range in thickness from 5 micrometers to several centimeters. In one embodiment, the spacer is about 75 micrometers in thickness.

EXAMPLE 10 Tunable Photonic Crystal Device

In one example, the tunable photonic crystal device comprises a film having a structural scaffold made of an ordered array of silica microspheres and a crosslinked network of polyferrocenylsilane (PFS), an iron-based metallopolymer, as the polymer component. This latter component actively mediates the lattice spacing of the silica spheres through an electrochemically-driven swelling and shrinking process, as described above.

To manufacture this example, thin films of monodisperse silica spheres made by sol-gel polymerization were deposited on indium-tin oxide (ITO) as the working electrode coated on glass plates as the substrate, using convective self-assembly, as is known in the art. The voids between the silica spheres were then infiltrated by a low molecular weight polyferrocenylsilane with pendant unsaturated C═C bonds, to which was added a small amount of a multifunctional thiol and radical photoinitiator. UV irradiation generates chemical crosslinks between the polymer chains through a well-known thiol-ene reaction, leading to a metallopolymer network matrix, thus forming the film.

In the example, the working and counter electrodes may be indium-tin oxide (ITO) and they may be mounted on glass as the substrates. The electrodes may be spaced apart using a spacer such as a hot-melt ionomer spacer. The spacer may be a gasket, serving to seal the conductive solution inside the device and to align the working electrode and the counter electrode relative to each other. In this example, the spacer is Surlyn™, which may be cut to the desired shape, placed between the electrodes and then melted to stick the electrode together. The device may be filled with an organic solvent-based liquid electrolyte as the conductive solution by vacuum filling, and may be sealed with epoxy. In the example, the photonic crystal-gel network film 52 is about 3-5 micrometers in thickness, and the electrodes are spaced 10-1000 micrometers apart. The photonic crystal-gel composite film was made of silica microspheres in a PFS metallopolymer network.

In some uses, the electrical potential applied across the electrodes range from −10V to 10V. Voltages outside this range would also work with the device.

In this example, the device was found to be responsive to cyclical changes in electrical potential from −2.0V to 2.0V when each voltage was maintained for about 15 seconds. Although this example was tested using a square-shaped voltage profile, any voltage profile may be used.

The example device displayed color changes as the film swelled due to movement of the conductive solution as driven by the electrical potential. Influx of solvent from the conductive solution into the film caused an increase in the lattice spacing of the film, and this is manifested as a red-shift of the reflectance peak, similar to the photonic crystal composite materials described previously. The degree of swelling is influenced both by the solvent in the conductive solution as well as the degree of crosslinking in the film, this latter parameter determining the ultimate range of tunability.

Although this example was tested by controlling the applied voltage, it would be understood that the device is equally controllable by controlling the applied current. Other methods of controlling the electrical field applied to the device would also suffice, and would be known to a person skilled in the art.

FIGS. 18A-E shows the results of measurements made on the example described above, that is, using a silica-PFS composite photonic crystal-gel film in the device, with ITO electrodes. FIG. 18A shows reflectance spectra of the example device taken at a series of increasing voltage applications, indicating that the device has distinct reflectance at a range of wavelengths, as indicated by the reflectance peaks. The graph in illustrates how the reflectance peak gradually shifts through a given range when incrementally varying the applied voltage. The inset shows the dependence of the peak position on the applied voltage, showing a continuum of accessible colors. The voltages tested ranged from 0.0 to about 3.5V, however it would be understood that voltages outside of this range would be equally useable for the device. Although the device was shown to have reflectance wavelengths in the range of about 500 nm to about 650 nm, it would be understood that reflectance wavelengths outside of this range may be achieved by applying different voltages. As well, these results were attained for the example using the specific materials described above. Different ranges of response may be obtainable by varying the materials used in the device. While the reflectivity of in this example is modest, its magnitude can be increased by increasing the thickness of the film. The position and magnitude of the accessible tuning range depends both on the size of the microspheres used to manufacture the film, as well as on the degree of crosslinking (as discussed with respect to FIG. 18E) and to a lesser degree on the molecular weight of the polymer in the film.

FIG. 18B shows spectra of the example device showing reflection of all three primary colors (i.e., red, blue and green) upon incremental oxidation of the metal atoms in the metallopolymer network of the photonic crystal-gel film. By appropriately choosing the starting sphere size and crosslinker content, a single sample can be tuned to all 3 primary colors. Hence, this device may be used to provide full-color displays as in current televisions systems—that is, by combining different amounts of the three primary colors. As already discussed, however, one advantage of this device is that it can be controlled to display a selected color directly, without using a combination of primary colors. Once a particular voltage was applied the reflectance peak shift was complete within 1-2 seconds, but data was collected after application of the voltage for 2 minutes to ensure that equilibrium had been reached. It is important to note that the reflected wavelength can also switched into the near-infrared region, rendering the materials transparent and providing a black or white state depending on the background. Although the graph shows a decrease in % reflectance as the wavelength increases, it would be understood that this trend is not limiting, and may be corrected by using different materials in the device, or by making modifications to the device as will be discussed further below.

FIG. 18C shows the Bragg reflectance peak maximum vs. number of cycles for a series of 100 oxidation-reduction cycles on the example device. The voltage was cycled between 2.0 V and −2.0 V, holding the device at the particular voltage for approximately 15 seconds to ensure equilibrium. The cycling stability of the materials was found to be good. As can be clearly seen, the peak maximum shifts reversibly, with its position returning to within nanometers after each voltage application. The electrical bi-stability of this device was evaluated by applying an initial voltage pulse to red-shift the reflectance peak, then disconnecting the device from the electrical source and measuring the drift of the peak in time. These results indicate that the device provides repeatedly stable results, and is robust for repeated uses. Although each voltage was held for about 15 seconds, this length of time is not required for the device to respond.

In general, the response time of the device can range from milliseconds to hours, and may depend on the applied electrical potential. Typically, as the applied voltage or current increases, the response time decreases because there is a greater driving force for removing or adding charge to the photonic crystal-gel film.

FIG. 18D shows an electrical bistability measurement carried out on the example device. The device was oxidized at 2.0 V, after which the electrical source was disconnected from the electrodes and the wavelength position of the reflectance peak monitored as a function of time. As can be seen from the graph, the device is capable of maintaining the reflectance wavelength without a continued application of electrical potential for at least 80 minutes.

FIG. 18E shows dependence of the maximum tunable wavelength range on the crosslinker content of the polymer in the photonic crystal-gel film. As the molar % of crosslinker in the polymer increases, increasing crosslinks are formed in the polymer and hence the rigidity of the polymer increases. This results in a corresponding decrease in the ability of the polymer to expand and contract. Hence, as the amount of crosslinker is increased, the ability of the device to shift its reflectance wavelength decreases. This result suggests that a person skilled in the art would be able to select a desired amount of crosslinker in the polymer so as to achieve a desired sensitivity in the tunable photonic crystal device.

In this example, the expansion in the lattice of the photonic crystal-gel film occurred mainly perpendicular to the electrode due to covalent anchoring of the film to the working electrode. However, this may not be the case where the film is free-floating, is merely supported by the electrode, or where the electrode is elastic.

Multi-Pixel Photonic Crystal Device

The device described above may also be modified to provide a multi-pixel device. By multi-pixel is meant that a single device can have multiple sections that have different tunable responses. In some embodiments, each section may be separately tunable. In the multi-pixel device, the components are similar to that of the single photonic crystal device. However, there is a plurality of working electrodes on which the photonic crystal sits.

In one embodiment, the multi-pixel device comprises a photonic crystal-gel film, counter electrode, and conductive solution as described previously. In addition, the multi-pixel device comprises a plurality of working electrodes, and an electrical potential can be separately applied to each. To apply separate potentials to each working electrode, there may be one connection to an electrical source, such as a potentiostat, for each working electrode, or there may be a single electrical source with switchable connections to each working electrode.

In some embodiments, the multi-pixel device may have a film that comprises multiple separate photonic crystal-gel film sections supported by a single working electrode. In this embodiment, each separate section comprises a different polymer with each with different tunable properties, such that each film section swells or shrinks to different amounts in response to the same electrical potential. Hence, application of an electrical potential between a single working electrode and the counter electrode will still result in different responses in each film section.

In one embodiment, multi-pixel devices were built and tested. This was achieved by depositing composite photonic crystal-gel films onto an array of working electrodes, which in this example consisted of 0.3 mm wide ITO strips on a glass substrate. In this way, each strip could be individually addressed by connecting it in a circuit to the counter electrode. Alternating dark green and red stripes could be produced in this example by applying a voltage to every other line in the array of working electrodes. When a higher voltage is applied to each of the activated lines, their color could be shifted out of the visible wavelength range, making them transparent. This transparency allows the black backing to be seen, and provides a dark state. Multicolor lines are also possible by applying different voltages to individual lines. The color tuning range can be shifted to lower wavelengths by using smaller microspheres in the film. It was found that applying an electrical potential to each individual electrode strip results in a change in reflectance wavelength of the photonic-crystal film immediately above that electrode strip. It can be readily appreciated that although the film on top of the electrode array is continuous, only the area directly over the contacted electrode is oxidized or reduced when a voltage is applied. This means that multi-pixel arrays may be manufactured without the need for patterning or segmenting the photonic crystal-gel film.

The possible materials and dimensions for each component of the multi-pixel device are the same as described previously. It would be understood that the size of each pixel may be dependent on the size of the electrode, as reflectance wavelength shifts in a section of the photonic crystal-gel film is affected by the working electrode it rests on. In this embodiment, the size of the pixels may be in the micrometer range, for example, 100 micrometers×100 micrometers or smaller. Typically, separate electrodes for the pixels are fabricated using photolithography, so the size limitations for pixels are limited only by this technology. For large applications, such as in billboards, where such a fine resolution is not required, each pixel may be of the size of 1 square inch or larger.

In another embodiment, pixels may be defined independent of the size of the working electrode. In this embodiment the counter electrodes and the working electrodes are arranged in a nonparallel arrangement, that is, one counter electrode overlaps more than one working electrode, thus one counter electrode forms multiple intersections with multiple working electrodes. Each intersection between a working electrode and a counter electrode defines a pixel, which may be selected by applying an electrical potential to the respective working and counter electrodes, thus activating the film section corresponding to that pixel. This allows the multi-pixel device to be simplified by reducing the number of individually activated electrodes. To improve the response of individual pixels, there may be multiple spacers used to separate the pixels from each other. The spacers confine the conductive fluid to a single pixel, thus preventing unwanted activation of a neighboring pixel. The spacers may be formed by creating wells, depressions, or holes in the spacer material. The wells, depressions, or holes may then be filled with the conductive solution.

Applications

In some embodiments of the above-described device, the photonic crystal-gel film is flexible, for example where the composite material is a silica-polymer. By using flexible electrodes, which may be mounted on flexible substrates (e.g., ITO electrodes coated on PET sheets), the entire device may be made to be flexible, such as for use in electronic paper. This allows the device to be integrated into flexible display components. It has been found that flexibility of the device does not significantly affect performance as compared to rigid devices (e.g., ITO electrodes mounted on glass substrate).

Electrically tunable photonic crystal devices, as described above, may provide electronic displays with certain attractive characteristics. In contrast to some other display technologies, these devices can reflect color whose wavelength is voltage tunable throughout the visible range without need for expensive color filters or sub-pixellation of red-green-blue elements, thereby wasting much less of the accessible light output.

Other modifications to the tunable photonic crystal device may provide further applications. One modification is to manufacture a combination of optical layers and controlled internal disorder into the photonic crystal-gel film, as is done in the manufacture of cholesteric liquid crystal displays (CLCDs). This modification increases the viewing angle of the reflected wavelength. Methods of improving the viewing angle using optical layers are discussed in U.S. Pat. No. 6,680,792, the entirety of which is hereby incorporated by reference. Methods of controlling internal disorder are known to persons skilled in the art, and have been used in devices by Kent Displays™.

Another modification is the implementation of a color mixing technique such as lateral integration or vertical integration, such as that used in Qualcomm's iMoD™ displays and in CLCDs, respectively. This modification would improve control over the saturation and lightness of the color from the device. Hue selection of the device may be simply controlled by selecting the electrical potential applied to the device. Methods of color mixing using vertical integration are discussed in U.S. Pat. No. 7,061,559, the entirety of which is hereby incorporated by references. Methods of color mixing using lateral integration are discussed in U.S. Pat. No. 6,680,792, previously incorporated by reference.

The bi-stability and low operating voltage of the tunable photonic crystal device may offer power requirements compatible with a number of applications such as outdoor and indoor signage, portable electronics, architectural panels, active camouflage and full-color electronic paper. Because the reflected wavelength of the device is not limited to the visible spectrum, this device may also be used for modulating UV, visible, or infrared light reflection and transmission.

The device can be used to achieve a display that is bright in high light environments, has electrical bi-stability, low operational voltage, can be integrated onto flexible substrates, and allows a continuous range of colors to be accessed without the need for color filters or optical elements.

As used herein, the terms “comprises”, “comprising”, “includes” and “including” are to be construed as being inclusive and open ended, and not exclusive. Specifically, when used in this specification including claims, the terms “comprises”, “comprising”, “includes” and “including” and variations thereof mean the specified features, steps or components are included. These terms are not to be interpreted to exclude the presence of other features, steps or components.

The foregoing description of the embodiments of the invention has been presented to illustrate the principles of the invention and not to limit the invention to the particular embodiment illustrated. It is intended that the scope of the invention be defined by all of the embodiments encompassed within the following claims and their equivalents. 

1. A tunable photonic crystal device comprising: a working electrode and a counter electrode forming a cell space there between; a conductive solution filling the cell space, the conductive solution comprising charged particles and a solvent; and a wavelength tunable photonic crystal film in the cell space, the film comprising: an ordered array of first constituents having a first refractive index embedded within a polymer network having a second refractive index different than the first refractive index, the ordered array of first constituents having a lattice spacing giving rise to a reflected wavelength, the polymer network being expandable and contractible in response to controlled uptake and expulsion, respectively, of at least one of the charged particles and the solvent by the polymer network, the reflected wavelength being dependent on the lattice spacing and the lattice spacing being tunable by expansion and contraction of the polymer network, the amount of uptake and expulsion of at least one of the charged particles and the solvent being tunable by controlling an electronic configuration of the polymer network; the device being adapted to be connected to an electrical source for applying an electrical potential between the working and the counter electrodes to control the electronic configuration of the polymer network.
 2. The device of claim 1 wherein the film is supported by the working electrode.
 3. The device of claim 1 wherein the working and the counter electrodes are each mounted on respective substrates.
 4. The device of claim 1 further comprising a spacer between the working and the counter electrodes to form the cell space.
 5. The device of claim 4 wherein the spacer is a non-conductive material selected from the group consisting of: thermoplastic polymer films, adhesive-coated plastic films, adhesives, epoxies, and spacer beads mixed into an adhesive or an epoxy.
 6. The device of claim 1 wherein there is a plurality of working electrodes arranged in an array and the electrical source is adapted to apply separate electrical potentials to each working electrode, individual sections of the film being supported by a respective working electrode to form individual pixels, each pixel being individually tunable by the electrical potential applied to the respective working electrode.
 7. The device of claim 1 wherein there is a plurality of working electrodes and a plurality of counter electrodes, each counter electrode arranged to overlap at least two working electrodes, individual sections of the film corresponding to an intersection of one working electrode with one counter electrode defining individual pixels, each pixel being individually tunable by the electrical potential applied between the one working electrode and the one counter electrode.
 8. The device of claim 7 wherein individual pixels are separated from each other by a plurality of spacers, the spacers preventing flow of conductive solution between pixels.
 9. The device of claim 1 wherein the working and the counter electrodes and the film are flexible.
 10. The device of claim 1 wherein the first and second electrodes is selected from the group consisting of: a conductive oxide, a conductive ceramic, and a carbon electrode.
 11. The device of claim 1 wherein the polymer network contains metal atoms selected from the group consisting of titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, niobium, molybdenum, ruthenium, rhenium, platinum, palladium, and rhodium, zinc, and combinations thereof.
 12. The device of claim 11 wherein the metal atoms chemically integrated into the polymer backbone are connected together directly or through linking units or combinations thereof.
 13. The device of claim 12 wherein the linking units are selected to impart pre-selected chemical, physical, electrochemical, optical and electronic properties to the polymer network.
 14. The device of claim 12 wherein the linking units are selected from the group consisting of substituted or unsubstituted carbanions, conjugated carbanions, linear olefins, cyclic olefins, acetylenes, phosphines, amines, carbonyls, carbenes, alkoxides or combinations thereof.
 15. The device of claim 12 wherein the metal atoms chemically integrated into the polymer backbone bear side-chain ligands which are selected from the group consisting of substituted or unsubstituted carbanions, conjugated carbanions, linear olefins, cyclic olefins, acetylenes, phosphines, amines, carbonyls, carbenes, alkoxides or combinations thereof.
 16. The device of claim 12 wherein the cross-links in the metallopolymer network is one of chemical bonds, physical bonds, nanoparticles, surfaces, hydrogen bonds, coordination bonds, electrostatic interactions, hydrophobic interactions, fluorophobic interactions and phase-separated domains or combinations thereof.
 17. The device of claim 12 wherein the cross-links in the cross-linked metallopolymer network are electronically conducting or electronically insulating.
 18. The device of claim 11 wherein the polymer network has segments in which the metal atoms are connected directly to each other to impart pre-selected chemical, physical, electrochemical, optical and electronic properties to the polymer network.
 19. The device of claim 1 wherein the polymer network has a preselected number density and distribution of crosslinks throughout the photonic crystal film.
 20. The device of claim 1 wherein the polymer network is formed from the polymerisation of a metal-containing monomer selected from the group consisting of bridged metallocenophanes.
 21. The device of claim 20 wherein the bridged metallocenophanes are substituted sila-1-ferrocenophanes.
 22. The device of claim 19 wherein the substituted sila-1-ferrocenophanes are selected from the group consisting of dialkylsila-1-ferrocenophanes, allcylalkoxysila-1-ferrocenop-hanes, dialkoxysila-1-ferrocenophanes, cycloalkylsila-1-ferrocenophanes, diarylsila-1-ferrocenophanes, alkylarylsila-1-ferrocenophanes, alkylalkenylsila-1-ferrocenophanes, alkylalkynylsila-1-ferrocenophanes or combinations thereof, and a metal-containing crosslinker selected from the group consisting of cyclobutylsila-1-ferrocenophane, sila-1,1′-diferrocenophane, 1,2-bis(methylsila[1]-ferrocenophane)acetylen-e, 1,4-bis(methylsila-[1]-ferrocenophane)benzene, bis(methylsila-[1]-ferro-cenophane)-1,4-diethynylbenzene, and 1,2-bis(methylsila[1]-ferrocenophane)-ethane or combinations thereof.
 23. The device of claim 1 wherein the polymer network is formed from the polymerisation of a mixture of compounds including about 50-100 weight % monomer, 0-30 weight % crosslinker, and 0-20 weight % initiator.
 24. The device of claim 1 wherein the polymer network is a polymer selected from the group of polyferrocenylsilanes.
 25. The device of claim 1 wherein the cross-linked metallopolymer network has a pre-selected porosity.
 26. The device of claim 1 wherein the first constituents include microparticles selected from the group of spheres, ellipsoids, rods, sphere containing polyhedra, cubes, and polyhedra, having cross-sectional dimensions from about 60 nanometers to about 100 micrometers.
 27. The device of claim 26 wherein the first constituents are assembled into a crystal having a pre-selected three-dimensional shape.
 28. The device of claim 27 wherein the crystal is single-crystalline or poly-crystalline.
 29. The device of claim 1 wherein the first constituents include substantially monodisperse microspheres having diameters from about 60 nanometers to about 100 micrometers.
 30. The device of claim 1 wherein the first constituents include substantially monodisperse microspheres selected from the group consisting of insulators, polymers, metals, and semiconductors or combinations thereof.
 31. The device of claim 1 wherein the first constituents include substantially monodisperse microspheres made of silica.
 32. The device of claim 1 wherein the first constituents include substantially monodisperse microspheres selected from the group consisting of polystyrene and polymethylmethacrylate.
 33. The device of claim 1 wherein the first constituents are voids filled with a pre-selected gas of a predetermined pressure.
 34. The device of claim 1 wherein the first constituents are formed as a thin film in the form of a predetermined pattern on a film substrate selected from the group consisting of metals, insulators, semiconductors, semimetals, polymers, and liquids or combinations thereof.
 35. The device of claim 1 wherein the first constituents are formed as a free-standing monolith structure.
 36. The device of claim 1 wherein the first constituents are modified to increase adhesion between the first constituents and the polymer network.
 37. The device of claim 1 wherein the first constituents are formed on a film substrate that is modified to increase adhesion between the substrate and the polymer network as well as to increase adhesion between the first constituents closest to the film substrate with the film substrate and the polymer network.
 38. The device of claim 1 wherein the first constituents form a face-centered cubic arrangement in the photonic crystal film.
 39. The device of claim 1 wherein the polymer network comprises a polymer selected from the group consisting of: polypyrrole, polythiophenes, and polyaniline.
 40. The device of claim 39 wherein the polymer network comprises polypyrrole or polythiophene electrodeposited among the first constituents.
 41. The device of claim 39 wherein the polythiophenes is a polyethylenedioxythiophene complex with polystyrenesulfonate).
 42. The device of claim 1 wherein at least one of the working electrode and the counter electrode is made from a conductive material selected from the group consisting of: conductive oxides, conductive ceramics, and carbon electrodes.
 43. The device of claim 42 wherein the carbon electrode is selected from the group consisting of graphite, amorphous carbon, and carbon nanotubes.
 44. The device of claim 1 wherein the reflected wavelength is in the range of: visible spectrum, ultraviolet spectrum, infrared spectrum, or combinations thereof.
 45. A method of tuning the device of claim 1, comprising: applying the electrical potential between the working electrode and the counter electrode to change the electronic configuration of the polymer network; and maintaining the electrical potential to tune the reflected wavelength from a first wavelength to a second wavelength.
 46. The method of claim 45 wherein the electrical potential is in the range of −100V to 100V.
 47. A display device comprising the tunable photonic crystal device of claim
 1. 48. The display device of claim 47 wherein the display device is selected from the group consisting of: digital signage, display screens, electronic paper, building panels, and camouflage.
 49. The display device of claim 47 wherein the electrical source is portable and the display device is a portable electronic. 